Yucera Materials Dental A1A2A3 Preshaded ST-Color Zirconia Block
Natural Color Transition, No Need Dyeing
Pre Shaded Zirconia Blocks made of nanometer medical grade zirconia
powder. The powder are firstly compacted by cold isostaticpressing
with high compressive strength and then pre-sintered to a certain
degree to offer good machinability.
UT zirconia blocks can be used to create crowns, bridges, inlays
and veneers of fixed partial denture with different translucency
levels and colors.
Zirconia Block Introduction
ST color Pre Shaded Zirconia Blocks
1. super translucency with total light transmission rate >50%
(comparable to lithium disilicate)
2. Average strength over 800 Mpa (can be used in a variety of
all-ceramic restorations such as onlay/inlay, crown, bridge and so
on)
3. Highly accurate Vita standard coloring liquid to meet the
requirements of high standard dental restoration
4. Excellent machinability owing to unique shaping technique
5. Top quality medical-grade nanometer zirconia powder
6. Ok for Anterior + Posterior teeth
Yurucheng zirconia block has high strength, excellent permeability
and color aesthetic repair effect that suitable for CAD/CAM system
and manual system.
Pre Shaded Zirconia Blocks Features
Safety:No irritation,No corrosion,Good bio-compatibility
Beauty:Natural teeth color can be reproduced
Comfortability:Low thermal conductivity,hot and cold changes do not
stimulte the pulp
Durability:Over 1600MPa perturbed strength, durable and useful
Sintering
Every batch of zirconia block has gone though a completely
sintering test. The sintering methods have a great impact on
blocks’ properties, such as translucency, dyeing results, strength,
hardness and ageing resistance, which will affect the blocks’ final
stability. Therefore, please follow the sintering curve of it.
HT/ST Sintering Curve (1-5)
HT/ST Sintering Curve (1-5) |
Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
Step 1 | 20 | 300 | 30 | 9.3 |
Step 2 | 300 | 1200 | 150 | 6 |
Step 3 | 1200 | 1530 | 110 | 3 |
Step 4 | 1530 | 1530 | 120 | 0 |
Step 5 | 1530 | 800 | 100 | -7.3 |
Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
HT/ST Sintering Curve (10 units)
HT/ST Sintering Curve (10 units) |
Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
Step 1 | 20 | 300 | 30 | 9.3 |
Step 2 | 300 | 1200 | 190 | 4.7 |
Step 3 | 1200 | 1530 | 150 | 2.2 |
Step 4 | 1530 | 1530 | 120 | 0 |
Step 5 | 1530 | 800 | 120 | -6 |
Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
ST Color Pre Shaded Zirconia Blocks
* Pre-shaded technics
* Uniform color
* Without post dyeing posses
* Suitable for full contour crown, bridge and anterior
Indications
Crown, Inlay, Onlay, 2-5 unit Bridges, Anterior
Physical Characteristics
Physical Characteristics |
Sintered density 6.07±0.01g/cm³ |
Bending Strength 1100 MPa |
Transmittance 45% |
Hardness 1200HV |
Sintering temperature 1480~1550℃/recommend 1530℃ |