1200 Mpa HT Dental Zirconia Block CAD Cam Peek Disc For Denture
Teeth
1200Mpa High bending strength HT detnal zirconia block cad cam
dentale for denture teeth and dental crown material
Introduction of YUCERA's HT high translucent dental zirconia:
YUCERA's comprehensive all-ceramic concept offers solutions at the
highest estheticlevel, while at the same time providing easy and
reliable workability. Whether you want quick results or are geared
up for partial veneering or full customization –we have the right
material for you. Our dental zirconia block perfect balance between
translucency and strength for the production of aesthetic
all-ceramic restorations.
Yucera's smart veneering concept suitable for both aesthetic and
production environments utilizing core masses and multiple effect
powders for all ceramic restorations
Features of SHT Multilayer high translucent strong zirconium oxide
for fixed and implant-supported prosthetics:
1. Outstanding aesthetics – high translucent and high strength.
2. Optional color – 20 colors ( 16 A-D, 3 Bleach).
4. 1200 MPa Bending Strength of zirconia disc.
5. 43% Translucency of zirconia disc.
6. Excellent esthetics, Maximum shade fidelity, Reliable,
reproducible results and Easy processing
Indications for veneered and fully contoured restorations made of
YUCERA's HT dental zirconia block/blank/disc
This type block can be used in veneered restorations, implant
abutments and telescope crowns, framework materials and fully
contoured restorations.
Processing Options
1. Monolithic processing or partial ceramic veneering
2. Optional brush or dipping infiltration possible
You can dye to what you wanted colors, contains:
A1, A2, A3, A3.5, A4;
B1, B2, B3, B4;
C1, C2, C3, C4;
D2, D3, D4
OM1, OM2, OM3
Packaging
Single Disc
YUCERA all series
| Type | Code | Translucency | Bending Strength | Hardness | Color | Size |
| White zirconia block | HT | 40% | ≧1200Mpa(Av.) | 1200HV | White (coloring liquid with vita 16 shades and 26
shades | Open system& Zirkon zahn system & Amann Girrbach System |
ST
| 43% | ≧1200Mpa(Av.) | 1200HV |
| Preshaded zirconia block | ST-Color | 43% | ≧1100Mpa(Av.) | 1200HV | Vita 16 shades and BL1, BL2, BL3 |
| Multilayer preshaded zirconia block | SHT-ML | 46% | ≧900Mpa(Av.) | 1200HV |
| UT-ML | 49% | ≧600Mpa(Av.) | 1200HV |
| 3D Plus-ML | 43%-57% | ≧700Mpa(Av.)--1050Mpa(Av.) | 1200HV |
Suitable for below system
| Open Cadcam System | Zironzahn System | Amann Girrbach |
| 98x10mm | 95x10mm | / |
| 98x12mm | 95x12mm | AGx12mm |
| 98x14mm | 95x14mm | AGx14mm |
| 98x16mm | 95x16mm | AGx16mm |
| 98x18mm | 95x18mm | AGx18mm |
| 98x20mm | 95x20mm | AGx20mm |
| 98x22mm | 95x22mm | AGx22mm |
| 98x25mm | 95x25mm | AGx25mm |
| HT/ST/ST-Color Sintering Curve |
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 300 | 30 | 9.3 |
| Step 2 | 300 | 1200 | 150 | 6 |
| Step 3 | 1200 | 1530 | 110 | 3 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 800 | 100 | -7.3 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |