| Trademark | Nominal Composition(%) | HRC | Application |
| B | C | Cr | Fe | Mo | Si | W | Ni | Others |
| WLNi-63 | 3.0 | 0.6 | 15.0 | 4.0 | | 4.5 | | Bal. | | 58-61 | Excellent abrasion and corrosion resistance. |
| WLNi-62 | 3.2 | 0.7 | 15.5 | 4.0 | | 4.2 | | Bal. | | 56-64 | shafts, sleeves, pump plungers, sucker rod couplings, bed knives,
camshafts, bushings, mill guides, mixer blades, seal rings, brick
manufacturing equipment, and conveyor screws. |
| WLNi-705 | 1.5 | 2.2 | 7.0 | 2.0 | | 2.3 | 48.1 | Bal. | | 56-63 | protection from severe sliding abrasion. Used on screw conveyors
and augers |
| WLNi-750 | 1.6 | 3.0 | 6.8 | 2.0 | | 1.5 | 48.0 | Bal. | Co: 6.0 | 57-63 | A tough nickel-chromium-tungsten matrix alloy is used to hold
extremely hard tungsten-carbide particles. Best used for the most
severe abrasive conditions. Finished by grinding. |
| WLNi-225 | 0.8 | | | | | 2.3 | | Bal. | P:2.0 | 13-17 | For glass container mould protection and restoration. Also used for rebuilding automotive parts (clutch components). |
| WLNi-226 | 0.8 | | | | | 2.2 | | Bal. | P:1.9
| 16-21 | Blow heads, edges and repairs blow-blow plungers, guide rings, baffles |
| WLNi-227 | 1.1 | | | | | 2.8 | | Bal. | P:2.1 | 22-27 | For glass container mould protection and restoration. Also used for rebuilding automotive parts (clutch components). |
| WLNi-234 | 1.0 | 0.15 | 4.0 | | 3.0 | 2.8 | | Bal. | P:2.1 | 32-36 | For glass container mould protection and restoration. |
| WLNi-4 | 2.1 | 0.4 | 10.0 | 2.8 | | 2.4 | | Bal. | | 35-40 | Aircraft gas turbines, steam turbine power plants, turbochargers
and valves in reciprocating engines, prosthetic devices, heat
treating equipment, pollution control equipment, coal gasification
and liquefaction systems, and components in pulp and paper mills. |
| WLNi-7631-60F | 1.16 | 2.58 | 6.08 | 1.80 | | 1.82 | 57.66 | Bal. | | | Aircraft gas turbines, steam turbine power plants, turbochargers
and valves in reciprocating engines, prosthetic devices, heat
treating equipment, pollution control equipment, coal gasification
and liquefaction systems, and components in pulp and paper mills. |
| WLNi-42 | 2.0 | 0.4 | 10.0 | 2.5 | | 3.0 | | Bal. | | 35-40 | Less hardness and slightly less abrasion and corrosion resistance. |
| WLNi-22 | 1.0 | 0.1 | 0.05 | 0.03 | | 3.0 | | Bal. | | 28-33 | Bottle moulds, cast iron parts |
| WLNi-22-KW | 1.0 | 0.1 | 0.05 | 0.03 | | 3.0 | | Bal. | P:2.0 | 28-32 | Aircraft gas turbines, steam turbine power plants, turbochargers
and valves in reciprocating engines, prosthetic devices, heat
treating equipment, pollution control equipment, coal gasification
and liquefaction systems, and components in pulp and paper mills. |