Wire To Wire Connector Terminals Crimp Terminals With Tinned
Phosphor Bronze Contact
1, The specification of the product including basic size
information, electrical and mechanical properties.
| Basic size information |
| Termination Interface Style | Crimp or compression |
| Processing methods | E-stamping before tin-plated or Gold-flash |
| Insulation O.D. | 1.85mm(Max) |
| Ordering code | C3030F-TPE-A or C3030F-GPE-A ; C3030M-TPE-A, C3030M-GPE-A, |
| Application | Power, wire to wire |
|
| Electrical properties |
| Current Rating | 5A AC, DC |
| Voltage Rating | 250V AC, DC |
| Contact Resistance | 10mΩ Max |
| Insulation Resistance | 1000MΩ min |
| Withstanding Voltage | 1500V AC/minute |
|
| Mechanical properties |
| Temperature range | -25℃ to 85 ℃ |
Other information please kindly check the following picture.
|
2, Related drawing and report
The following pictures are engineering drawing and testing report
for your reference, wish these can help you to purchase the ideal
and right parts from us. Thank you!
Environmental Performance And Others
| Test Description | Procedure | Requirement |
| 6-1 | Temperature Rise | Carrying rated current load.(Based upon UL 498) | 30℃(Max.) |
| 6-2 | Heat Resistance | 85±2℃,96 hours (Based upon JIS C0021/MIL-STD-202 Method 108A Cond.
A) | Appearance No Damage. Contact Resistance 20mΩ (Max.) |
| 6-3 | Cold Resistance | -25±3℃,96 hours (Based upon JIS C0020) |
| 6-4 | Humidity | Temperature: 40±2℃ Relative Humidity : 90~95% Duration: 96 hours (Based upon JIS C0022/MIL-STD-202 Method 103B Cond. B) | Appearance No Damage. Contact Resistance 20mΩ (Max.) Insulation Resistance 100MΩ (Min.) Dielectric Withstanding Voltage Must meet 4-3 |
| 6-5 | Temperature Cycling | 5 cycles of: a) -55℃ 30 minutes b) +85℃ 30 minutes (Based upon JIS C0025) | Appearance No Damage. Contact Resistance 20mΩ (Max.) |
| 6-6 | Salt Spray | Tin-plated 12 hours / Gold- plated 24 hours exposure to a salt
spray from the 5±1% solution at 35±2℃. (Based upon JIS
C0023/MIL-STD-202 Method 101D Cond. B) |
| 6-7 | SO2 Gas | 24 hours exposure to 50±5ppm. SO2 gas at 40±2℃. |
| 6-8 | NH3 Gas | 40 minutes exposure to NH3 gas evaporating from 28% Ammonia
solution. |
| 6-9 | Solderability | Soldering Time: 5±0.5 sec. Solder Temperature: 245±5℃ | Solder Wetting 95% of immersed area must show no voids, pin holes |
| 6-10 | Resistance to Soldering Heat | Solder pot method Soldering Time: 10±0.5sec. Solder Temperature: 260±5℃ Solder iron method Soldering Time: 5±0.5 sec. Solder Temperature: 370℃ ~ 400℃ | Appearance No Damage. |
3,Our Services:
1. Note
We have many type of products , pls sent your own drawing or
picture for our reference .So that we can provide the quotation and
spec more precisely and promptly.
2. Samples and Freight Charge
we can provide samples free for customer test, but for our company
policy, you can give us the freight collect number, such as Fedex
,TNT,UPS and so on .Or you can pay about $40 to our paypal account,
and once you order from us next time, we can deduct USD40 in the
amount immediately .Pls note our sample is same as our spec, and
the goods will be exactly same with samples.
3. Lead time
we will sent out the items within 5 days after we received the
payment. Of course, we can negotiated with you if the order is need
urgently.
4. The terms of payment
T/T, Western Union, Paypal for small amount.