0Cr21Al6 resistance wire is widely used in industrial and
electrical fields, mainly in heating elements, resistors,
thermocouples, and more.
0Cr21Al6 resistance wire is widely used in electric heating
products, mainly providing heating functions.
An electric kettle is a common application of 0Cr21Al6 resistance
wire. The resistance wire is installed at the bottom or side of the
kettle and heats the water when powered on. This design allows for
quickly heating water to the desired temperature, providing users
with hot water conveniently.
0Cr21Al4 resistance wire is used in the thermal control systems of
aerospace devices to maintain temperatures within safe limits.
An electric blanket is a heating product placed on a bed, typically
used during cold seasons or by individuals needing extra warmth.
0Cr21Al6 resistance wire is woven into the fabric of electric
blankets, generating heat when powered on to create a comfortable
sleeping environment for users.
A heat gun is a tool used for applications such as heat shrinking
and soldering. The heating element in heat guns often utilizes
0Cr21Al6 resistance wire to produce high-temperature hot air for
heating and soldering tasks.
A dryer is a household appliance used for drying clothes, shoes,
etc. 0Cr21Al6 resistance wire is used as the heating element in
dryers, either by generating hot air or directly contacting the
surface of items to accelerate the drying process.
In addition to the mentioned products, 0Cr21Al6 resistance wire is
also applied in various other electric appliances such as thermos
flasks, coffee pots, ovens, etc., providing heating functions for
users' convenience in daily life.
- Ferrous Chromium Aluminum alloy performance tables
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest |
| | | | | | Nb0.5 | Mo1.8-2.2 |
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | |
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |