CBN-E10 is a lubricant, mold release agent, and mold release agent
for various high-temperature operations. Such as glass industry,
mold protection, metal welding industry, etc., This product can
effectively lubricate and isolate the interface, making the
processing process smoother.
The sintering of metal and ceramic powders is usually carried out
on a graphite plate. After the layer of boron nitride, the
contamination, reaction and bonding of carbon on the sintered parts
that may occur at the sintering temperature can be obviously
removed.
Boron nitride is also suitable for welding and furnace brazing
processes. The surface of the workpiece can be protected to avoid
the spatter of welding slag provides excellent welding protection.
The boron nitride coating can also protect the surface of the
welding nozzle of metal welding wire, inert gas shielded welding
and metal active gas welding from spattering of welding slag.
This product is based on boron nitride, and its unique formula
makes this product perform very well in high temperature protection
and lubrication, effectively improving production efficiency and
product quality.
Features
Environmental protection: boron nitride is an environmentally
friendly material, non-toxic and zero pollution
Chemical vvproperties: In high temperature environment, strong
non-stick, good lubrication and release effect
Product features: high temperature lubricant, high temperature
protection antioxidant
Technical Specification
| Items | Cersol-BN-E10 |
| Main Component | Hexagonal boron nitride |
| Covering area | 15-25m/L |
| Binder | Clay |
| Viscosity | 1000- 1200CPS |
| Solid content | 15-20% |
| Specific Gravity | 1.0- 1.2(g/cm3) |
| Color Appearance | W hite milky |
| PH | 3 — 5 |
| Shelf Life | One Year |
| Condensation point / fire point | -2℃ |
Application
glass industry
mold protection
metal welding industry
special ceramic powder sintering
Precaution
1. When coating, the surface of the coating should be clean to
avoid leaving oil and dust to ensure that the coating can adhere.
2. The coating material needs to be preheated to 70- 150℃, the
insufficient temperature will affect the coating effect.
3. The spray thickness is about 15-30μm.
4. Boron nitride release agent BN-E10 has strong adhesion
properties, and it has obvious lubricating protection effect
without coating too thick .
5. After spraying, it can be used after drying (can be dried at 300
℃).
6. The coating can be washed with water directly.
7. After drying, wipe off the dust on the coated surface with a
soft cloth such as silk.