EN 1.4319 Stainless Steel Plates and Sheets 0.4 - 20.0mm Cold
Rolled & Hot Rolled X5CrNi17-7
Quick Informations
| Products Name | 1.4319 Stainless Steel Plate | Standard | EN 10088-2 |
| Thickness | 0.4 - 20.0mm | Surface | 2B NO.1 |
| Standard Size | 1000*2000mm 1219*2438mm 1500*6000mm | Brand | TISCO BAOSTEEL POSCO |
More Informations of our Products
| Item | Stainless Steel Plates / Stainless Steel Sheets |
| Main Grades | 201, 202, 301, 304, 304L, 310S, 309S, 316, 316L, 321, 409L, 410,
410S, 420, 430, 904L, etc. |
| Standard | ASTM GB JIS EN DIN BS |
| Thickness | 0.4mm-40mm |
| Stock Thickness | 0.4mm 0.5mm 0.6mm 0.8mm 1.0mm 1.2mm 1.5mm 2mm, 2.5mm, 3mm, 3.5mm,
4mm, 4.5mm, 5mm, 5.5mm, 6mm, 7mm, 8mm,10mm,12 - 40mm |
| Width | 1000mm 1219mm 1500mm or cutting any size as request |
| Standard size | 1000*2000mm 1219*2438mm 1500*6000mm 2000*6000mm |
| Finish | 2B, BA, No. 1, No. 4, mirror, brush, hairline, chequered, embossed,
etc. |
| Package | Standard export package |
Advantage of 1.4319 Stainless Steel
- Better rust and corrosion resistivity than type 301.
- Good cryogenic resistance.
- Excellent ductility.
- Slightly less attractive in looks than type 301.
- Decent hot strength.
Grade 301L / 1.4319 / UNS S30103 / SUS301L
1.4319 stainless steel (UNS S30103) is also an austenitic steel
type that has a normal composition featuring 17% chromium along
with 7% of nickel.
The 1.4319 stainless steel is slightly better in terms of corrosion
resistance because it has slightly fewer carbon contents. But the
301L also offers good ductility. It is not as strong as the 301,
though.
It very well for various jobs involving forming, drawing as well as
welding. Just like grade 301, the 1.4319 is also available in
various conditions, including full hard, ½ hard, and ¼ hard
conditions. 1.4319 Stainless steel is slightly inferior to 301 in
terms of temperature resistivity and also has a low melting range.
When cold working it the 1.4319 stainless steel will become
magnetic, but just like the 301 steel, it is also non-magnetic when
annealed.
Chemical Composition of 1.4319 Stainless Steel
The 1.4319stainless steel has 0.03% carbon with 2% manganese. There
is 0.045% of phosphorus in the mix, along with 1% of silicone and
0.03% of sulfur.
As we have mentioned above that the chromium content in this mix is
17%, while the nickel content is 7%. With around 0.2% of the
nitrogen in the composition, the formula for 301L stainless steel
is complete.
Grade
Content | Grade 301L | UNS S30103 | JIS G4305 | DIN 1.4319 |
|---|
| Carbon, C | 0.03 | 0.03 | 0.03 | 0.03 |
| Manganese, Mn | 2.0 | 2.0 | 2.0 | 2.0 |
| Silicon, Si | 1.0 | 1.0 | 1.0 | 1.0 |
| Phosphorous, P | 0.045 | 0.045 | 0.045 | 0.045 |
| Sulfur, S | 0.030 | 0.030 | 0.030 | 0.030 |
| Chromium, Cr | 16-18 | 16-18 | 16-18 | 16-18 |
| Nickel, Ni | 6.0-8.0 | 6.0-8.0 | 6.0-8.0 | 6.0-8.0 |
| Nitrogen, N | 0.20 | 0.20 | 0.20 | 0.20 |
| Molybdenum, Mo | - | - | - | - |
Mechanical Properties:
The 1.4319 stainless steel is frequently used in its annealed and
cold-rolled forms. Being in a work-hardened state, it develops and
improves tensile strength. It is not as good as the strength of 301
stainless steel, but it is better than most within the austenitic
category.
At room temperature, the minimum mechanical properties of 301L as
per A666 and ASTM A240 standards are,
| Form | Elongation in 2 inches (minimum) | Tensile strength (minimum) | Yield strength (minimum 2%) |
| Annealed | 45% | 80 Ksi | 550 MPa | 35 Ksi | 220 MPa |
| ¼ Hard | 30% | 130 Ksi | 870 MPa | 80 Ksi | 530 MPa |
| ½ Hard | 22% | 170 Ksi | 1104 MPa | 130 Ksi | 770 MPa |
| ¾ Hard | 16% | 185 Ksi | 1307 MPa | 145 Ksi | 1031 MPa |
| Full Hard | 12% | 190 Ksi | 1426 MPa | 160 Ksi | 1265 MPa |
Applications of 1.4319 Stainless Steel
- Rail cars.
- Pressure vessels
- Convertor components
- Utensils and appliance parts.
- Door and drainage parts.