75g Synthetic Paper / Hot Melt Glue / 80G White Glassine Liner
Frozen Label Low Temp Label
1. Features of QYMN High Adhesive Label
■ Really high adhesion adhesive glue, developed by adjust the
adhesive element percentage and technology, Not only by add more
adhesive GSM glue.
■ It is suitable for high speed die cutting.
■ After made into blank label, it can be printed by thermal
transfer ribbon.
■ Suitable for different kind of substrate, like bags, wall, steel
and so on.
■ Adhesive material is from USA or Japan, which can ensure the
adhesive quality.
■ Quality is more stable, Different order quality is 100% same as
we have strict quality control policy.
2. Introduction of High Adhesive Label
High Adhesive Label is specially used to make label for rough
surfaces substrate. It has good adhesion performance to uneven
surface and even curved surface, such as woven bags, walls, boards,
cardboard boxes, etc
QYMN High Adhesive Label has good initial adhesion and perfect
durable adhesion. It is one kind of permanent adhesive made of hot
melt glue.
QYMN High Adhesive Label has two model, QA model and TB model.
3. TDS
| Facestock | Liner |
| Material | 75g Synthetic Paper | Material | 80G White Glassine Liner |
| Thickness | mm | 0.08±0.002 | Thickness | mm | 0.1±0.005 |
| Basic Weight | g/m2 | 80±2 | Basic Weight | g/m2 | 85±2 |
| Tensile Strength | N/25mm | | Tensile Strength | N/25mm | ≥55.0 |
| Extensibility | % | | Extensibility | % | ≤13.0 |
| Smoothness | | Good | Smoothness | | Good |
| Printability | | Good | Peeling Force | g/25mm | 10--15 |
| Specification |
| Adhesive | Hotmelt Glue | Peeling Force at 180. | N/25mm | 20 |
| Adhesive Thickness | mm | 0.02±0.002 | Suitable Temperature | ℃ | -25--60 |
| Adhesive Amount | g/m2 | 20±2 | Recommended Temperature | ℃ | -20--50 |
| Ring initial stickiness | N/25mm | 16 | Durability | H | ≥50 |
| Remark 1,Testing Condition:23.C+2.C,50%+5%RH; |
| 2,Advised storage temperature 23.C,50%RH, Avoid Sunshine, for 1
year |
| 3,Spec only for reference, not as delivering standard |