Structural Strengthening Carbon Fiber Adhesive With High Tensile
Strength
Carbon Fiber Primer
Carbon Fiber Leveling Adhesive
Carbon Fiber Reinforced Polymer
Structural Strengthening Carbon Fiber Adhesive With High Tensile
Strength
Xinchor CFRP Carbon Fiber Adhesive is Low viscosity, strong
penetration ability, used for smearing of the underlayer of
reinforced members' surface, the role is penetration bonding
reinforcement to the broken concrete after chiseling off; of the
surface of members was intact, smearing was not needed.
Application Range
Load increases
Seismic reinforcement
Improve structural state
Damage of structural parts
Change the structural function
Remit mistakes in design and construction
Flexural strengthening,
Shear strengthening,
Column confinement and ductility improvement.
Load Increases
Increased live loads
Increased traffic volumes on bridges
Installation of heavy machinery in industrial buildings
Vibrating structures
Changes of building utilization
Seismic Strengthening
Column wrapping
Masonry walls
Damage to Structural Parts
Aging of construction materials
Vehicle impact
Fire
Blast resistance
| Testing project | Standard | Result |
| Lot#1 | Lot#2 | Lot#3 |
| Tensile Strength | ≥38 Mpa | 46.7 | 48.6 | 47.6 |
| Tensile modulus of elasticity | ≥2400 MPa | 2437 | 2484 | 2473 |
| Elongation | ≥1.5% | 2.79 | 2.80 | 2.63 |
| Bending Strength | ≥50Mpa (no fragmental damage) | 91.0 | 88.8 | 84.9 |
| Compressive Strength | ≥70 Mpa | 77.6 | 83.0 | 81.5 |
| Bonding Capacity | | |
| Steel-Steel Tensile Shear Strength | (23±2)℃, (50±5)%RH ≥14 Mpa | 14.3 | 14.9 | 14.2 |
| Steel-Steel bonding tensile strength | ≥40 Mpa | 40.7 | 40.1 | 41.1 |
| Steel-Steel T-impact peeling strength | ≤20 mm | 0 | 0 | 0 |
| Steel to C45 Concrete cohesive haul strength | ≥2.5 Mpa (Concrete cohesion damage) | 4.5 | 4.2 | 4.4 |
| Thermal deformation temperature | ≥65℃ | 65.8 | 66.1 | 66.4 |
| Non-volatile content | ≥99% | 99.5 | 99.5 | 99.5 |
| Thixotropy Index | ≥3mm | 3.3 | 3.2 | 3.2 |
| Ageing resistance to heat and humidity | Reduction rate of shearing strength ≤12% | 11.6 | 11.2 | 10.5 |
| Ageing resistance to heat | Reduction rate of shearing strength ≤5% | 3.9 | 4.7 | 4.0 |
| Resistance to alkaline medium | No reduction of strength and only destruction of concrete. without
any cracks, stripping, foaming on appearance | pass | pass | pass |
| Resistance to alkaline medium | No reduction of strength and only destruction of concrete. without
any cracks, stripping, foaming on appearance | pass | pass | pass |
| Resistance to freezing and thawing | Reduction rate of shearing strength ≤5% | 2.9 | 3.4 | 3.5 |
| Resistance to long term stress | No defect after steel to steel shearing, The deformation value of
creep ＜0.4mm | 0.2 | 0.1 | 0.2 |
| Resistance to salt spray | Reduction rate of shearing strength ≤5% | 4.1 | 4.5 | 4.1 |