Vacuum Sintering Furnace Using Silicon Molybdenum Rod 1800C For
Factory Producing
What is Silicon Molybdenum Rod?
Mosi2 heating element is a special product combined metal and
ceramics. So it has the characteristics of silicon and molybdenum.
Molybdenum disilicide (MoSi2) is a refractory metal silicide that
is primarily used as a heating element. In recent years, its
potential for use as a structural ceramic has been recognised, as
the material combines excellent oxidation resistance and high
elastic modulus at elevated temperatures.
Please tell us the following data of molybdenum disilicide MoSi2
rod heating element when send enquiry to us :
d = the diameter of hot zone ?
c = the diameter of cold zone ?
Le = the length of hot zone ?
Lu = the length of cold zone ?
a=Shank spacing?
How many pcs ?
It should be pointed out that element cannot be used for rather
long time in 500-1700°C, or it will be powdered owing to the strong
oxidizing action in low temperature.
Physical property of Silicon Molybdenum Rod :
| Density | Bending Strength | Hardness | Apparent Porosity | Water Absorption | Elongation | Fracture Toughness | Compressive Strength |
| 5.8g/cm3 | 350Mpa | 12.0Gpa | ±2% | 0 | 4% | 4.5Mpa.m1/2 | 650Mpa |
Silicon Molybdenum Rod technical data:
| 1700°C Grade | 1800°C Grade |
| d/c (mm) | 3/6 | 4/9 | 6/12 | 9/18 | 12/24 | 3/6 | 4/9 | 6/12 | 9/18 | 12/24 |
| Le Max,mm | 350 | 450 | 1400 | 1400 | 1700 | 350 | 450 | 1400 | 1400 | 1700 |
| Lu Max,mm | 300 | 450 | 1000 | 1000 | 1000 | 300 | 450 | 1000 | 1000 | 1000 |
| a (mm) | 25 | 25 | 40/50 | 60 | 80 | 25 | 25 | 40/50 | 60 | 80 |
| f (mm) | 25 | 25 | 45 | 75 | 100 | 25 | 25 | 45 | 75 | 100 |
| g (mm) | 15 | 15 | 25 | 30 | 40 | 15 | 15 | 25 | 30 | 40 |
Nonstandard shape & size could be made according to your
requirement |
Silicon Molybdenum Rod characters:
1. diameter:3/6mm;6/12mm;9/18mm;12/24mm
2. length:Lu length from 150 to 700mm,Le length from 150 to
600mm,customized is available .
3. operation temperature: from 500C to 1700.C .Max temperature can
up to 1800.C
4. shape : U type ; W type ;straight type ;L type
5. function: ceramic ,magnetic material,glass ,metallurgy
,fireproofing material furnace.
Mosi2 heating element consists of hot zone and cold zone, the
welding point is beautiful ,smoothly, without bump
The Advantages of Molybdenum Disilicide Heating Elements from SP :
1· Economical, clear and safe.
2· Superior oxidation resistance, low corrosion.
3· Little deformation and better radiance.
4· Long service life, easy installation and maintenance.
5· Efficiently apply a wide range of products and atmospheres
6. Our fast and professional transportation:
Packing and shipping :
Packaging Details: Packed with sponge and box case, and then put it into wooden case.
Port: Qingdao, Shandong
Lead Time: Shipped in 10 days after payment Transportation: Most by air.
Heating element installed in furnace