Customized Size Tungsten Carbide Seal Rings ISO9001 Certificated
Anti Corrosion
Making of tungsten carbide material, tungsten carbide bushing shows high hardness and transverse rupture strength, and it has
superior performance on resisting abrasion and corrosion, which
enable it to be widely used in many industries.
Base on different application of the users, tungsten carbide bushes
are usually made of different tungsten carbide grades. The major
two series of tungsten carbide grade is YG series and YN series.
Generally speaking, YG series tungsten carbide bushes have higher
transverse rupture strength, while YN series tungsten carbide bush
resist corrosion better than the former one.
Product Features:
• The precision seal ring is made of high quality materials by an
advanced process with several patented technologies
• The seal ring has a very complicated shapes, high accuracy,
stable mechanic properties
• It has much higher wear and corrosion resistance properties, and
a service life of more than twenty thousand hours in the normal
case
Grade and Recommended Application:
| Grade | Density
(g/cm³) | Hardness
(≥HRA) | Strength
(Mpa) | Recommended application |
| YG20 | 14.30-14.50 | 86.5 | 2500 | Maximum hardness,excellent wear resistance.Mostly for the last 1-2
stands of good high speed bars. |
| YG25 | 14.10-14.30 | 85.5 | 2520 | Higher wear resistance and moderate impact resistance in the
series.Mostly for the last 1-3 stands of good high speed bars. |
| YG30 | 13.90-14.10 | 84 | 2520 | Moderate wear resistance and impact resistance.Good for general
purpose.Used in the last 1-4 stands or all stands or finishing
mills. |
| YG40 | 13.60-13.80 | 83.5 | 2570 | Best for general purpose.Mostly for the front stands of good mills
and in the rear stands of common mills. |
| YG45 | 13.45-13.65 | 82.5 | 2570 | Used in the first and second stands of finishing mill and in the
stands of pre-finishing rolling mills . For every milling lines of
low speed rolling, low precision and unstable operation. |
| YG55 | 12.90-13.10 | 81 | 2570 | Maximum binder content in YGH series Good toughness and thermal
crackresistance. For every milling lines for low speed rolling, low
precision and unstable operation. Mostly for the stands of
pre-finishing rolling mills and hot rolling of cribbed steel. |
Parameter:
| ID | OD | H |
| 160 | 170 | 12 |
| 155 | 165 | 12 |
| 150 | 160 | 12 |
| 140 | 150 | 12 |
| 130 | 140 | 12 |
| 120 | 130 | 12 |
| 110 | 120 | 12 |
| 100 | 110 | 12 |
| 90 | 100 | 12 |
| 82 | 90 | 12 |
| 70 | 80 | 12 |
| 60 | 70 | 12 |
| 50 | 60 | 12 |
Why choose us?
Our factory can be customized production, Best production capability, Best quality
control, Best Service, Competitive price;
Reply within 24 hours and detail quotation;
Customized making according to your drawing papers;
Accept trial order and sample order;
100% QC inspection against shipment;