Tungsten carbide sand blasting nozzle ,water spray nozzles for
ceramics
Product Description
Our tungsten carbide waterjet nozzles inner tube is high finish
blast hole, and the use of our unique polishing technology pores to
keep the hardness of inside waterjet nozzles is same as the outside
of water jet nozzles. Comparing to other common tungsten water jet
nozzles:higher hardness, higher density, higher wear resistance,
higher stability.Consistent and long service life.
Material: Nano Carbide / ultrafine grain tungsten carbide
Density: 15.7g/cm³
Rockwell hardness: 96HRA
Size: as below and also can cutomize any size
Welcome to contact us to get the sample to test our waterjet nozzles good quality!
Please let us know the clear size including OD,ID & length(mm).
Weikeduo offers abrasive and flow control nozzles for every application:
• Abrasive Waterjet
• Dry Blasting
• Wet Blasting
• Suction Blast
• Mirco Abrasive
• Scrubber
• Descaling
• Slurry Jet
• Spray Drying
•Centrifuge
D7.14*d1.02*76.2mm water cutting sand blasting nozzle
sand blasting nozzle ,also name tungsten carbide water cutting,tungsten carbide sand
tube.it is mainly using to cutting metal,ceramic,stone,glass or other materials.
1.100% fresh material,we also coating tantalum tin for higher wear
resistance.
2. the common sizes are Φ6.35,Φ7.14,Φ7.6,Φ9.45 ect.
3. long life,the hardness up to 96.5HRa,execellent wear resistance.
4. also product according your sizes.
sand blasting nozzle ‘s spcifications:
Use superfine nanometer tungsten carbide particles, the
wear-resisting performance to the next level, superior
wear resistance makes it far beyond the ordinary tungsten carbide,The service life of the nozzle.Cobalt
content of less than 0.6%, density of 15.45 g/cm3 ~ 15.6 g/cm3,
bending 2000 mpa to 2400MPa.Super oxygen resistance, small thermal expansion coefficient,
unique high hardness and density, far beyond the other similar
products, the use of hard Alloy tube abrasion resistance stronger.
Sand tube due to high-speed abrasive particle erosion, its
selection is very important.Sand tube material, in general, must have high hardness, high
resistance Grinding, both be short of one cannot.Generally for tungsten carbide composite materials processing.Usually, cemented carbide, WC as the main
resistance,Grinding phase exists in the form of particles, CO, just as the
binder.
Use: widely used in various types machine, WHP type, FLOW type,
type JET, KMT, OMAX type, type WS.
Life: 150-300 hours refers to the general statistical time under 350
Mpa working pressure. The service life of sand mixing pipe is
determined not only by its own quality, but also by many factors,
such as working pressure, water column, abrasive (pomegranate
sand), knife head structure design and some human factors. Among
them, the influence of water column on the life of sand mixing pipe
is most easily ignored in practical application. water
| Dimensional parameters of water cutter sand pipe |
| ФD(mm) | Фd1(mm) | L(mm) | θ° | а° |
6.0 | 0.76 | 76.2 | 40 | 28 |
| 6.0 | 1.02 | 76.2 | 40 | 28 |
| 6.35 | 0.5 | 76.2 | 40 | 28 |
| 6.35 | 0.76 | 76.2 | 40 | 28 |
| 6.35 | 1.02 | 76.2 | 40 | 28 |
| 7.14 | 0.76 | 76.2 | 40 | 28 |
| 7.14 | 1.02 | 76.2 | 40 | 28 |
| 7.6 | 0.76 | 76.2 | 40 | 28 |
| 7.6 | 1.02 | 76.2 | 40 | 28 |
| 9.45 | 0.76 | 76.2 | 40 | 28 |
| 9.45 | 1.02 | 76.2 | 40 | 28 |
Welcome your inquiry.