Zinc Oxide Rotary Kiln Metallurgy Machine Rotary Kiln For Mining
1. Metallurgical chemical kiln introduction of metallurgy machine
Metallurgical chemical kiln is mainly used for magnetization
roasting of lean iron ore in metallurgical industry steel works;
Oxidation roasting of chromium and nickel ore; Refractory plant
roasted high metallurgical ore and aluminum plant roasted clinker,
aluminum hydroxide; Chemical plant roasted chrome ore and chromium
ore powder and other minerals.
In the research and development and the application in the field of
active lime kiln has achieved fruitful results, with advanced
equipment of calcining lab and industrial simulation lab, active
lime complete system technology and key equipment technology
reached the international advanced level, obtained many
achievements of science and technology and patent technology, in
various sectors such as steel, alumina, power plant desulfurization
has been applied.
2. Zinc oxide rotary kiln product parameters of metallurgy machine
| No. | Model (m ) | Figure number | SPEC | Main reducing gear | Main motor | Thrust Roller form | supporting bearing | Weight (t) | Note |
| Rev r/min | Slope % | Production capacity t/d | Type | Velocity ratio i | Type | Power kW | Rev r/min |
| *1 | Φ3.45×52 | J968 | 0.35 ～0.8 | 5 | 350 |
Worm gear drive reducer A=450,i=12 | | | 75 | | hydraulic pressure | roll | 412.5 | fexible drive A=3150,m=28,i=10.84
drive weight 32.6t7.5pt; (Including cover)i=10.84 |
| 2 | Φ4×58 | J978 | 0.35 ～3.5 | 5 | 400 | | | | 250 | | hydraulic pressure | slide | 341 | |
| 3 | Φ4.15×58.2 | J975 | 0.35 ～0.7 | 5 | 756 | | | | 55 ×2 | | hydraulic pressure | roll | 637 | fexible drive |
3. Zinc Oxide Rotary Kiln Process flow of metallurgy machine:
(1) The zinc charge and coking coal are crushed into particles less
than 40 mesh, and the zinc charge and coking coal are mixed at the
ratio of 1∶0.30 ~ 0.35 to get the mixture.
(2) Make the mixture into the particle mixture with an effective
diameter of 8-15 mm, and finally put the particle mixture into the
rotary kiln for smelting.
(3) When zinc oxide ore or industrial slag with zinc content of 15%
~ 25% is smelted to produce zinc oxide, coke or coal can be greatly
saved.
(4) The zinc oxide obtained by smelting has high productivity, good
product quality and small nodulation amount.
After-sales service
LUOYANG ZHONGTAI INDUSTRIES able to provide:
1. ENGINEERED SPARES - DESIGN AND MANUFACTURING
2. LARGE VOLUME STEEL AND IRON CASTING FOUNDARIES
3. HUGE MACHINE SHOP CAPABILITIES
4. TRAINING PROGRAMMES
5. PREVENTATIVE MAINTENANCE PROGRAMS
6. PREVETATIVE MAINTENANCE SERVICES
7. COMPREHENSIVE MAINTENANCE PROGRAMS