Alloy steel T5 T9 ASTM 213 ASTM A213 Steel tubes with alloy steel grade T5 T9
Torich is a manufacturer of T5 T9 boiler tubes in China for over 20
years.have losts experience on produce
it,Torich produce T5 T9 boiler pipes as per standard ASTM A213
,ASTM A213 Standard is American standards.
T5 and T9 tubes is a hot products .
ASTM A213 T5 Seamless tube spec
| Grade | ASME SA213 T5 and T9 |
| ASTM A213 T5 Tube size range | Outside diameter 0.19inch-7inch Wall thickness:0.102-0.787inch |
| SA213 GrT5 finned tubes | 0.62inch thickness fin tubes |
| Alloy steel SA213 T5 length | Fix length or random length |
| Surface of SA213 T5 | Black ,Gray |
| End of SA 215 T5 Alloy tubes | Plain |
| Testing on T5 tubing | Non destructive testing,Bending tesnt, UT,HT ,Impact Testing etc |
Supplier of T5 steel cold drawn in various shapes | Round,omega,Oval |
T5:
| Chemical compostion max % |
| C | Si | Mn | P | S | Cr | Mo |
| 0.15 | 0.50 | 0.30-0.60 | 0.025 | 0.025 | 4.0-6.0 | 0.45-0.65 |
ASTM Gr T5 Equivalent
SA213 T5 X11CrMo5+L1.7362
SA213 T5b X11CrMo5+NT1
SA213 T5c X11CrMo5+Nt2
T9:
| Chemical compostion max % |
| C | Si | Mn | P | S | Cr | Mo |
| 0.15 | 0.25-1.0 | 0.30-0.60 | 0.025 | 0.025 | 8.0-10.0 | 0.90-1.10 |
Other alloy steel grade is avaiable upon agreement!
Application:
ASTM A213 Standard Scope
1.1 This specification covers seamless ferritic and austenitic
steel boiler, superheater, and heat-exchanger tubes,
designated Grades T91, TP304, etc. These steels are listed in
Tables 1 and 2.
1.2 Grades containing the letter, H, in their designation, have
requirements different from those of similar grades
not containing the letter, H. These different requirements provide
higher creep-rupture strength than normally
achievable in similar grades without these different requirements.
1.3 The tubing sizes and thicknesses usually furnished to this
specification are 1/8 in. [3.2 mm] in inside diameter
to 5 in. [127 mm] in outside diameter and 0.015 to 0.500 in. [0.4
to 12.7 mm], inclusive, in minimum wall thickness
or, if specified in the order, average wall thickness. Tubing
having other diameters may be furnished, provided such
tubes comply with all other requirements of this specification.
1.4 The values stated in either SI units or inch-pound units are to
be regarded separately as standard. Within the
text, the SI units are shown in brackets. The values stated in each
system may not be exact equivalents; therefore,
each system shall be used independently of the other. Combining
values from the two systems may result in
non-conformance with the standard. The inch-pound units shall apply
unless the “M” designation of this specification
is specified in the order.
TABLE 1 Chemical Composition Limits, %A, for Low Alloy SteelA
Maximum, unless range or minimum is indicated.
Where ellipses (…) appear in this table, there is no requirement,
and analysis for the element need not be
determined or reported.
B It is permissible to order T2 and T12 with a sulfur content of
0.045 max. See 16.3.
C Alternatively, in lieu of this ratio minimum, the material shall
have a minimum hardness of 275 HV in the hardened
condition, defined as after austenitizing and cooling to room
temperature but prior to tempering. Hardness testing
shall be performed at mid-thickness of the product. Hardness test
frequency shall be two samples of product per
heat treatment lot and the hardness testing results shall be
reported on the material test report.