Metallurgical Slag Pot Slag Bowl Slag Ladle Castings And Forgings
For Mining Machinery
1. Metallurgical slag ladle castings and forgings product introduction
Slag ladle is the equipment used to load slag before steelmaking
furnace. Its use environment is bad, it is changeable when heated,
and it requires high use times. The larger the slag ladle volume,
the more difficult it is to cast.
Slag ladle is the place where iron and slag are produced. The
modern blast furnace iron extraction field is equipped with mud gun
(plugging machine), opening machine, swing flow groove, crane, iron
tank, slag ladle and other equipment. The mud cannon was pneumatic,
then electric.
2. Smelting and casting process of metallurgical slag ladle castings and forgings
Cupola smelting, single bale pouring, first fast then slow, one
pouring.
3.Slag pot,slag bowl,slag ladle castings and forgings technical parameters
| Product name | Slag pot,slag bowl,slag ladle castings and forgings |
| Material | DIN 17182 GS-16Mn5 1.1131 |
| Fact cubage | 22 CBM |
| Appro.Net Wt | 10 -100 t |
| Product application | Steel works |
| OEM service offered | According to customer’s drawings |
4. Influencing factors of slag ladle life
(1) Influence of abnormal slag of converter:
Although it is safe to carry steel slag in the cast steel slag
ladle, there is still a risk for abnormal slag of converter. The
abnormal slag of converter is mainly the slag of washing furnace
before dismantling and the slag of high temperature and high oxide
produced by smelting special steel. Furnace washing is to dissolve
the splashing slag layer and the adherent slag and charging
material on the converter lining through the high temperature slag,
so as to facilitate the subsequent furnace dismantling work. The
temperature of steel slag produced is higher than that of
conventional slag, the content of iron oxide in slag is higher, and
the fluidity is good. In the slag ladle after the iron oxide slag
and slag ladle body chemical reaction, coupled with the slag body
temperature load impact, it is likely to cause tank accident.
(2) Influence of casting residue in continuous casting:
Continuous casting bag besides part of steel slag, still contain
liquid steel, the temperature is higher than or close to the
melting point of cast steel, if the slag pot to do special
processing, when casting allowance is bigger, direct contact with
the molten steel slag pot body possible corrosion slag pot body
cause wear tank cast steel materials, the cooled or partial
corrosion adhesion sex cohere with the slag pot, It is easy to
damage the slag ladle when it is turned over.
(3) External blows to slag ladle damage:
When the slag ladle and the steel slag loaded in it have bonded,
leading to the normal can not turn over the tank, need to use the
gun car to continuously hit to help pour out the slag in the slag
ladle, the mechanical force in the process of beating in the form
of wave transfer in the slag ladle, and in the local formation of
superposition, resulting in the damage of the slag ladle.