China Factory Promotion Flat Lamination Bonding of Decorative
Panels PUR Hot Melt WANLI® PUR-XBB662-1 with Open Time 2~3 Minutes
@23℃ And Stable Viscosity, High Initial Bonding Strength, And High
Final Bonding Strength After Curing.
Wanli® PUR hot melt adhesive PUR-XBB662-1 for flat lamination
bonding is a single-component reactive PUR hot melt adhesive with
100% solid content. PUR-XBB662-1 can be used for mutual adhesion of
PET, PVC and other plastics. PUR-XBB662-1 is featured stable
viscosity under heating at a certain temperature, high initial
bonding strength and final strength. After curing, PUR-XBB662-1 has
good peel strength and good yellowing resistance.
APPLICATION
Wanli® PUR hot melt adhesive PUR-XBB662-1 is used for flat
lamination bonding. PUR-XBB662-1 can be used for mutual adhesion of
PET, PVC and other plastics.
| Application Material | Woodworking Flat Lamination Hot Melt Adhesives |
| Appearance | Transparent White / Solid |
| Component | PUR (Polyurethane) |
| Application Industry | Woodworking Flat Lamination Bonding |
| Solid Content | 100% |
| Operating Temperature | 110~150℃( Depend On Equipment, Substrate, Environment And Other Conditions) |
| Melt Viscosity | About 5000mPa·s@140℃(Brookfield-ASTMD3236) |
| Open Time | 2~3min@23℃ |
| Usage Scope | Flat Lamination Bonding of Wood, Foam and Aluminum Materials |
| Shelf Life | Half One Year |
| Package | 310ml/Aluminum Tube, 2Kg/Bag, 20Kg/Barrel, 200Kg/Barrel |
FEATURE
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final strength.
PUR-XBB662-1 has good peel strength and good yellowing resistance
after curing.
USER GUIDE
The package of PUR-XBB662-1 is suitable for various dispensing
equipment.
The recommended operating temperature is 110℃~150℃.
Place finished product in a working environment with suitable
temperature and humidity (recommended temperature: 23~25℃, about
65% relative humidity) to achieve complete curing.
STORAGE
Dry, cool, avoid direct sunlight, no more than 35℃.