BeCu Copper Rods C17300-H 1.0mmdia. x 2000mmL Used For Probe Pin
Product Description:
Name: BeCu copper rods
Grade: C17300
End Product Form: Rods/ Bars
Standard: ASTM B196, QQ-C-530
State of product: H(TD04)
Processing: Seamless / Welding
Feature: With high strength and high conductivity
Package: Pack in coil+waterproofing winding film+Drier+Wooden Case
Specification: 1.0mmdia. x 2000mmL
What are the Properties of BeCu Copper?
Properties of BeCu:
Beryllium copper is a ductile, machinable, and weldable alloy.
BeCu has an excellent response to precipitation-hardening
treatments.
BeCu has excellent thermal conductivity (62 Btu/ft-deg.F-H), and it
is about 3-5 times more conducting than Tool steel.
It shows resistance to stress relaxation.
It is resistant to non-oxidizing acids such as hydrochloric acid
(HCl) and carbonic acid (H2CO3), to plastic decomposition products,
to abrasive wear, and galling.
It can be heat-treated for increased strength, durability, and
electrical conductivity.
Beryllium copper displays the maximum strength (up to 1,400 MPa
(200,000 psi)) of any copper-based alloy.
CUBERYLLIUM ®-173 also named -C17300 (CDA 173) offers the strength properties of C17300 with the added benefit of
being “free machining”. C17300 rod and wire contain a small amount
of lead to provide an alloy tailored for automatic machining
operations. Lead promotes formation of finely divided chips thus
extending cutting tool life.
Chemical Composition of BeCu Copper C17300:
| CUBERYLLIUM® Brand | UNS-Number | Beryllium | Cobalt
+ Nickel | +Cobalt
+ Nickel
+ Iron | Pb | Copper |
| Cuberyllium-C173 | C17300 | 1.80-2.00 | 0.20 min | 0.6 max | 0.2～0.6 | Balance |
Note: Copper plus additions equal 99.5% minimum.
Typical Physical Properties of BeCu Copper C17300:
Density: 8.36g/cm3
Density before age hardening: 8.25g/cm3
Melting Range: 870~980℃
Elastic Modulus((kg/mm2 (103)): 13.4
Thermal Expansion Coefficient(20 °C to 200 °C m/m/°C): 17 x 10 -6
Thermal Conductivity(cal/(cm-s-°C)): 0.25
Mechanical and Electrical Properties of BeCu Copper Rod C17300:
| Temper(*) | Diameter | Heat Treatment | Tensile Strength ksi | Elogation Percent (Min) | Electrical Conductivity Percent IACS | Hardness Rockwell B or C Scale |
|---|
| A(TB00) | ALL SIZE | / | 400~600 | 30 | 15~19 | B45~85 |
H(TD04)
| 5~10 | / | 660~900 | 5 | 15~19 |
＞B88
|
| ＞10~25 | / | 620~860 | 5 | 15~19 |
| ＞25 | / | 590~830 | 5 | 15~19 |
| AT(TF00) | ALL SIZE | 3 hr 320°C | 1100~1380 | 2 | 22~28 | C35~42 |
| HT(TH04) | 5~10 | 2 hr 320°C | 1200~1550 | 1 | 22~28 | C37~45 |
| ＞10~25 | 1150~1520 | 1 | 22~28 | C36~44 |
| ＞25 | 1120~1480 | 1 | 22~28 | C35~44 |
Product Photo:
FAQ:
Q1: What’s the advantages the Beryllium Copper of CUBERYLLIUM®?
A1: 1: The Biggest Coil weight could be reach 1200kg/Coil.
2: We are the only one who melting by Vacuum semi-Continuous
Furnace.
3: Surface further polishing for top clients.
Q2: How about your payment terms?
A2: Generally, 30% as deposit by T/T, then 70% should be paid
before the delivery.
Q3: Why you melting by Vacuum semi-Continuous Furnace?
A3: Could be get the Cast ingot without gas,smaller segregation,
Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the
amount is different.