High Performance 1Mm Thickness 410 420J1 420J2 430 Stainless Steel Coil

410
Stainless steel 410 is produced according to American ASTM standard, equivalent to China's 1Cr13 stainless steel, S41000 (American AISI, ASTM).Carbon 0.15%, chrome 13%,410 stainless steel: good corrosion resistance, machinability, general purpose blade class, valve class.Heat treatment of 410 stainless steel: solid solution treatment (℃) 800-900 slow cooling or 750 fast cooling.Chemical composition of 410 stainless steel: C≤0.15,Si≤1.00,Mn≤1.00,P≤0.035,S≤0.030,Cr=11.50~13.50.
416
416 stainless steel is a kind of steel with good cutting performance in stainless steel. 416 stainless steel is mainly used in the production of solenoid valves, micro-special motors and electrical components.The above materials are free cutting stainless steel, especially suitable for automatic lathes, CNC lathes mass production.
C: 0.15 or lessMn: 1.25 or lessSi: 1.00 or lessCr: 12.0 ~ 14.0Ni: less than or equal to 0.60% nickel is allowedP: 0.06 or lessS: 0.15 or higherMo: molybdenum less than or equal to 0.60% can be added

420
420 stainless steel is a kind of martensitic stainless steel, with certain wear resistance and corrosion resistance, high hardness characteristics, suitable for all kinds of precision machinery, bearings, electrical, equipment, instruments, instruments, transportation vehicles, household appliances.
It is mainly used in manufacturing components that are resistant to corrosion by air, water vapor, water and oxidizing acid.
C: 0.16 ~ 0.25Mn: 1.00 or lessSi: 1.00 or lessCr: 12.0 ~ 14.0Ni (2) : 0.75 or lessP: 0.04 or lessS: 0.03 or less

430
430 stainless steel is a universal steel with good corrosion resistance, better thermal conductivity than austenite, smaller coefficient of thermal expansion than austenite, thermal fatigue, add stabilizing element titanium, welding seam mechanical properties.
430 stainless steel for building decoration, fuel burner components, household appliances, household appliances components.
The 430F is a type of steel with free cutting properties on 430 steel, mainly used in automatic lathes, bolts and nuts.
430LX adds Ti or Nb to 430 steel, reduces C content, improves processing performance and welding performance, mainly used for hot water tank, heating water system, sanitary appliances, household durable appliances, bicycle flywheel and so on.
Because of its chromium content, it is also called 18/0 or 18-0.
Compared with 18/8 and 18/10, the chromium content is slightly lower and the hardness is correspondingly lower.
chemical component:
(C) :≤0.12%
(Si) :≤0.75%
(Mn) :≤1.00%
(P) :≤0.040%
(S) :≤0.030%
(Ni) :≤0.60%
(Cr) :16.00~18.00%

440C
440C steel is a martensitic stainless steel.
Carbon content 1.0%, chromium content 16-18%.
Strong rust resistance, is high - quality stainless steel.
Scope of application: mainly used for manufacturing bearing parts in corrosive environment and strong oxidation atmosphere without lubrication.
The 440C has good dimensional stability at high temperature, so it can also be used as corrosion-resistant high temperature bearing steel.
In addition, it can also be used to make high-quality knives, such as surgical knives, scissors, nozzles, bearings and so on.
The capacity of 440C to bear dynamic load is low
chemical composition
C: 0.95 ~ 1.20
Si: 1.00 or less
Mn: 1.00 or less
S: 0.030 or less
P: 0.035 or less
Cr: 16.00 ~ 18.00
Ni: allowable content ≤0.60

Chemical composition and mechanical properties of stainless steel