CuBe2 Strips on Coil 0.10x8mm, 0.35x8mm With MTC 3.1 Certificate
Product Normal Description:
Product Name: Strips
Quality: CuBe2, DIN. 2.1247
Certificate: MTC 3.1
Product Specification: 0.1x8mm, 0.35mmx8mm
State: Half hard rolled
Product Brand: CUBERYLLIUM®
Chemical Composition of CuBe2 Alloys:
| Numbering | Be | Co+Ni | Cu | Fe | Pb | Si | Al |
| C17200 | 1.8-2.0 | ≥0.2 | Margin | 0.15 | - | 0.15 | 0.15 |
Temper Designations of CuBe2 Strip:
| Cuberyllium Designation | ASTM | Mechanical and Electrical Properties of Copper Beryllium Strip |
| Designation | Description | Tensile Strength
(Mpa) | Yield Strength 0.2% offset | Elongation Percent | HARDNESS
(HV) | HARDNESS
Rockwell
B or C Scale | Electrical Conductivity
(% IACS) |
| A | TB00 | Solution Annealed | 410～530 | 190～380 | 35~60 | <130 | 45~78HRB | 15～19 |
| 1/2 H | TD02 | Half Hard | 580～690 | 510～660 | 12~30 | 180~220 | 88~96HRB | 15～19 |
| H | TD04 | Hard | 680~830 | 620~800 | 2~18 | 220~240 | 96~102HRB | 15～19 |
| HM | TM04 |
Mill hardened | 930～1040 | 750～940 | 9～20 | 270～325 | 28～35HRC | 17～28 |
| SHM | TM05 | 1030～1110 | 860～970 | 9～18 | 295～350 | 31～37HRC | 17～28 |
| XHM | TM06 | 1060～1210 | 930～1180 | 4～15 | 300～360 | 32～38HRC | 17～28 |
Tipical Uses of CuBe2 Alloys:
Oil & Gas - Instrument Housings, Flex Shafts, MWD & LWD Components,
Bearings, Bushings, Valve Components, Pump Shafts
Automotive - Plastic Molds, Electronic Components, RWMA Tooling
Electrical - Spring Connectors, Current Carring Navigational
Instruments, Contact Bridges, Clips, Relay Parts, Electrical Switch
and Relay Blades
Aerospace - Landing Gear Bushings, Aircraft Components, Cryogenics
Fasteners - Bolts, Screws, Retaining Rings, Lock Washers,
Belleville Washers, Roll Pins, Fasteners, Washers
Other Industrial - Flexible Metal Hose, Non Sparking Safety Tools,
Shafts, Pump Parts, Rolling Mill Parts, Bearings, Bushings, Valve
Seats, Valve Stems, Wear Plates on Heavy Equipment, Springs,
Electrochemical
Specifications of CuBe2 Alloys:
| Strip | ASTM B194 |
| Bar | ASTM B196 |
| Wire | ASTM B197 |
| Plate | ASTM B194 |
| Sheet | ASTM B194 |
| Tube | ASTM B643 |
Product Photo of CuBe2 Strips:
Excellent Properties of CuBe2 Alloys:
Key Technology of Beryllium Copper(Heat treatment)
Age Hardening
Age hardening significantly enhances the material’s strength. This
reaction is generally carried out at temperatures between 260°C and
540°C depending on alloy and desired characteristics. This cycle
causes the dissolved beryllium to precipitate as a beryllium rich
(gamma) phase in the matrix and at the grain boundaries. It is the
formation of this precipitate which causes the large increase in
material strength. The level of mechanical properties attained is
determined by the temperature and time at temperature. It should be
recognized that beryllium copper has no room temperature aging
characteristics.