Ceramic tank Zirconia ball mill tank Alumina ball mill tank high
temperature tank
Description:
There are four ball grinding tanks on a turntable. When the
turntable rotates, the ball grinding tank rotates around the
turntable axis and rotates around its own axis in the reverse
planetary rotation movement. The grinding balls and materials in
the tank collide and rub each other in high speed movement to
achieve the purpose of crushing, grinding, mixing and dispersing
samples.
Principal characteristic of Ceramic tank Zirconia ball mill tank Alumina ball mill tank high
temperature tank:
1 High wall finish, not easy to stick material.
2. Strong oxidation resistance, acid and alkali resistance.
3. Excellent corrosion resistance
4. Good intergranular corrosion resistance
5. High temperature resistance is also better.
6. High wear resistance and long service life.
7. High grinding efficiency.
Application of Ceramic tank Zirconia ball mill tank Alumina ball mill tank high
temperature tank:
Ultrafine grinding equipment, fine chemical industry, electronic
paste, semiconductor, new energy, nano new materials, medical
instruments, precision casting, structural ceramics, refractory
materials, electronic communications, sensitive ceramics,
petrochemical industry, aerospace, machinery manufacturing, optical
fiber connector, battery materials and other high-precision end
fields
Technical Parameters:
| Specification | Outer diameter | inner diameter | Bottom diameter | Height | Cover thickness |
| 50ML | 64 | 50 | 64 | 56 | 12 |
| 100ML | 74 | 60 | 64 | 68 | 12 |
| 250ML | 94 | 80 | 89.5 | 88 | 13 |
| 500ML | 103 | 89 | 89.5 | 100 | 13 |
| 1L | 130 | 114 | 119.5 | 118 | 13 |
| TIPS:The size list is for reference only, the above is the standard
size of conventional products,specialspecifications can be
customized . |
| Item | unit | Typical Values |
| Composition | (wt%) | 94.8%ZrO2+5.2%Y2O3(wt%) |
| Color | - | White |
| Density | g/cm3 | 6.03 |
| Water absorption | ％ | 0 |
| flexure strength | MPa | 1250 |
| HV hardness | GPa | 1300 |
| Modulus of Elasticity | GPa | 210 |
| Poisson's ratio | - | 0.31 |
| fracture toughness | MPa m1/2 | 8-10 |
| thermal expansivity | [normal temperature～400℃] x10-6 | 10.3 |
| Thermal conductivity | W/(m.K) | 3 |
| nitric acid(90%) | weight loss | 0 |
| sulfuric acid(95%) | 0.03 |
| sodium hydroxide(30%) | 0.07 |
Advantages:
1). Excellent electrical insulation;
2). High hardness;
3). Relatively low strength and fracture toughness;
4). Resistance to wear and corrosive;
5). Excellent thermal stability;
6). Resistance to high temperatures;
7). High electrical resistivity;
8). Good chemical stability and resistance.