CW102C Free Machining Copper Beryllium Round Bar As Per EN 12164
For Switch Parts
Product Description:
Name: Free machining copper beryllium round bar
Grade: CW102C
Size: according customers' requirement
End Product Form: Rods/ Bars
Standard: ASTM B196, QQ-C-530
State of product: A(TB00),H(TD04),AT(TF00),HT(TH04)
Processing: Seamless / Welding
Feature: With high strength and high conductivity
Package: Pack in coil+waterproofing winding film+Drier+Wooden Case
| Weight % | Be | Ni+Co | Ni+Co+Fe | Pb | Cu | Other |
|---|
| Minimum | 1.80 | 0.2 | - | 0.2 | Bal | - |
|---|
| Maximum | 2.00 | - | 0.60 | 0.60 | 0.5 |
|---|
Note: Copper plus additions equal 99.5% minimum.
Typical Physical Properties of CW102C Free Machining Copper Beryllium Alloys:
Density: 8.36g/cm3
Density before age hardening: 8.25g/cm3
Melting Range: 870~980℃
Elastic Modulus((kg/mm2 (103)): 13.4
Thermal Expansion Coefficient(20 °C to 200 °C m/m/°C): 17 x 10 -6
Thermal Conductivity(cal/(cm-s-°C)): 0.25
Mechanical and Electrical Properties of CW102C Free Machining Copper Beryllium Round Bar:
| Temper(*) | Diameter | Heat Treatment | Tensile Strength ksi | Elogation Percent (Min) | Electrical Conductivity Percent IACS | Hardness Rockwell B or C Scale |
|---|
| A(TB00) | ALL SIZE | / | 400~600 | 30 | 15~19 | B45~85 |
H(TD04)
| 5~10 | / | 660~900 | 5 | 15~19 |
＞B88
|
| ＞10~25 | / | 620~860 | 5 | 15~19 |
| ＞25 | / | 590~830 | 5 | 15~19 |
| AT(TF00) | ALL SIZE | 3 hr 320°C | 1100~1380 | 2 | 22~28 | C35~42 |
| HT(TH04) | 5~10 | 2 hr 320°C | 1200~1550 | 1 | 22~28 | C37~45 |
| ＞10~25 | 1150~1520 | 1 | 22~28 | C36~44 |
| ＞25 | 1120~1480 | 1 | 22~28 | C35~44 |
Product Photo:
CW102C Free Machining Copper Beryllium Alloys International
Specification:
Rods/Bars/Tubes: ASTM B196, QQ-C-530
Wires: ASTM B197, QQ-C-530
European Standards: CuBe2Pb, Alloy M25, UNS.C17300, DIN.2.1248,
CW102C to EN
Note:
ASTM: American Society for Testing and Materials
SAE: Society of Automotive Engineers
AMS: Aerospace Materials Specification(Published by SEA)
RWMA: Resistance Welder Manufacturers' Association
Note: Unless otherwise specified, material will be produced by
ASTM.
Key Technology of Beryllium Copper(Heat treatment)
Age Hardening
Age hardening significantly enhances the material’s strength. This
reaction is generally carried out at temperatures between 260°C and
540°C depending on alloy and desired characteristics. This cycle
causes the dissolved beryllium to precipitate as a beryllium rich
(gamma) phase in the matrix and at the grain boundaries. It is the
formation of this precipitate which causes the large increase in
material strength. The level of mechanical properties attained is
determined by the temperature and time at temperature. It should be
recognized that beryllium copper has no room temperature aging
characteristics.
FAQ:
Q1:What’s the advantages the Beryllium Copper of CUBERYLLIUM®?
A1: 1: The Biggest Coil weight could be reach 1200kg/Coil.
2:We are the only one who melting by Vacuum semi-Continuous
Furnace.
3:Surface further polishing for top clients.
Q2: How about your payment terms?
A2: Generally, 30% as deposit by T/T, then 70% should be paid
before the delivery.
Q3: Why you melting by Vacuum semi-Continuous Furnace?
A3:Could be get the Cast ingot without gas,smaller segregation,
Grain Refinement