CuBe2Pb Leaded Beryllium Copper Bars 8*1000mm For Contact Bridge
Product Description:
Name: Leaded beryllium copper bars
Grade: CuBe2Pb
Size: 8*1000mm, or according customers' requirement
End Product Form: Rods/ Bars
Standard: ASTM B196, QQ-C-530
State of product: A(TB00),H(TD04),AT(TF00),HT(TH04)
Processing: Seamless / Welding
Feature: With high strength and high conductivity
Package: Pack in coil+waterproofing winding film+Drier+Wooden Case
CUBERYLLIUM® manufactures copper beryllium in several distinct compositions.
These fall into two categories: alloys selected for high strength
(Alloys 172,173,170) and alloys selected for high conductivity
(Alloys 751,750,741). And Gost standard QBe2,QBe1.9Ti for Russia
Market. Also Supply Master alloy : CuBeryllium-200;
CuBeryllium-275);CuBeryllium-350 and Cuberyllium-400 to global
factory.
Beryllium copper has its reasonable share of common names. You will
listen referred to as BeCu, Copper Beryllium, Beryllium Bronze, and
Spring Copper. Anytime you hear those terms, they're in reference
to Beryllium Copper. Beryllium round bars are accessible as high
strength and high conductivity alloys.
CUBERYLLIUM ®-173 also named -C17300 (CDA 173) offers the strength properties of C17300 with the added benefit of
being “free machining”. C17300 rod and wire contain a small amount
of lead to provide an alloy tailored for automatic machining
operations. Lead promotes formation of finely divided chips thus
extending cutting tool life.
Chemical Composition of CuBe2Pb Leaded Beryllium Copper Alloys:
| CUBERYLLIUM® Brand | UNS-Number | Beryllium | Cobalt
+ Nickel | +Cobalt
+ Nickel
+ Iron | Pb | Copper |
| Cuberyllium-C173 | C17300 | 1.80-2.00 | 0.20 min | 0.6 max | 0.2～0.6 | Balance |
Note: Copper plus additions equal 99.5% minimum.
Typical Physical Properties of CuBe2Pb Leaded Beryllium Copper Alloys:
Density: 8.36g/cm3
Density before age hardening: 8.25g/cm3
Melting Range: 870~980℃
Elastic Modulus((kg/mm2 (103)): 13.4
Thermal Expansion Coefficient(20 °C to 200 °C m/m/°C): 17 x 10 -6
Thermal Conductivity(cal/(cm-s-°C)): 0.25
Mechanical and Electrical Properties of CuBe2Pb Leaded Beryllium Copper Bars:
| Temper(*) | Diameter | Heat Treatment | Tensile Strength ksi | Elogation Percent (Min) | Electrical Conductivity Percent IACS | Hardness Rockwell B or C Scale |
|---|
| A(TB00) | ALL SIZE | / | 400~600 | 30 | 15~19 | B45~85 |
H(TD04)
| 5~10 | / | 660~900 | 5 | 15~19 |
＞B88
|
| ＞10~25 | / | 620~860 | 5 | 15~19 |
| ＞25 | / | 590~830 | 5 | 15~19 |
| AT(TF00) | ALL SIZE | 3 hr 320°C | 1100~1380 | 2 | 22~28 | C35~42 |
| HT(TH04) | 5~10 | 2 hr 320°C | 1200~1550 | 1 | 22~28 | C37~45 |
| ＞10~25 | 1150~1520 | 1 | 22~28 | C36~44 |
| ＞25 | 1120~1480 | 1 | 22~28 | C35~44 |
CuBe2Pb Leaded Beryllium Copper Alloys International Specification:
Rods/Bars/Tubes: ASTM B196, QQ-C-530
Wires: ASTM B197, QQ-C-530
European Standards: CuBe2Pb, Alloy M25, UNS.C17300, DIN.2.1248,
CW102C to EN
Note:
ASTM: American Society for Testing and Materials
SAE: Society of Automotive Engineers
AMS: Aerospace Materials Specification(Published by SEA)
RWMA: Resistance Welder Manufacturers' Association
Note: Unless otherwise specified, material will be produced by
ASTM.
Service We Could Offer:
| High Quality | Well trained workers, with more than 10 years' experience. |
|---|
| Quick Response | Your inquiry will be replied within 24 hours. |
|---|
| Competitive Price | Products provided directly from our factory with good price. |
|---|
| Flexibility | Small orders or sample orders are acceptable for quick delivery. |
|---|
| Delivery Time | Usually 3-7 days for sample orders, 15-25 days for quantity orders. |
|---|
| OEM | We could provide end products according to customers; drawings,
samples or designs. |
|---|
Product Photo:
Key Technology of Beryllium Copper(Heat treatment)
Age Hardening
Age hardening significantly enhances the material’s strength. This
reaction is generally carried out at temperatures between 260°C and
540°C depending on alloy and desired characteristics. This cycle
causes the dissolved beryllium to precipitate as a beryllium rich
(gamma) phase in the matrix and at the grain boundaries. It is the
formation of this precipitate which causes the large increase in
material strength. The level of mechanical properties attained is
determined by the temperature and time at temperature. It should be
recognized that beryllium copper has no room temperature aging
characteristics.