Electrophoretic coating for domestic microwave oven
Product Introduction :
HS-6060ALB/HS-6600 White Cationic Epoxy Electrocoat for auto is a
new generation electrophoretic coating researched and developed by
HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating
that is environment-friendly with high property and low cost. Such
coating does not contain heavy metal like lead, tin, cadmium and
mercury etc. It is a two-component, water-dispersed
resin,meanwhile, it took in features of previous products, and can
adapt galvanized steel sheet perfectly, almost can be applied to
foundation coating of all metal, such as: cold and hot rolled steel
sheet, galvanized steel sheet, aluminum products, zinc-aluminum
alloy sheet and stainless steel sheet etc.
This product features shown below:
Excellent leveling coating,good bonding force and compatibility
with plastic powder.
Strong anti-corrosion properties, good salt spray resistance
workpiece edge.
Good stability of bath can adaptable for a longer updating cycl
Main ingredients:
Pigment: titanium dioxide, kaolin,antirust pigment
| Neutralizing agent: organic acid |
Additives: surface active agent, prevent shrinkage cavity
agent,resistance to yellowing agent
|
Product quality data
| Project | Technical data | Test standard |
Resin
(HS-6060ALB) | White Paste (HS-6600) |
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±400 | —— | HG/T 3334 |
| Appearance | —— | Milky white liquid | White viscous liquid,no agglomeration | Visual |
| Storage stability |
No stratified state, and there were no obvious difference compared
to before storage | In 5-35 ℃ temperature 1 year |
Note: pH, conductivity measurement in the resin/pure water = 1:1
dilution
Filling tank proportion and method
⑴ Bath preparation
Ratio:
Resin 750.00-1000.00
Paste 250.00
DI water 1900.00-2200.00
Total 3 3025.00-3575.00
⑵ Ripening conditions
Sample quantity: 3000-4000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-34 ℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(165-175)℃×(20-30)min (Keeping temperature of
parts coated)