Take magnesium oxide board machinery asia for example:
1.Capacity :
2million sqm/300 days (basis of
calculation:L:2440mm,T:8mm,W:1220mm,
weight:7kg/M2)
2. Automation: semi degree automatic and high degree automatic
3. Main materials:
MgO,MgCl2,Fiberglass cloth,Non-woven cloth,Sawdust/perlite
4. MGO board specification:
length(mm)
| 2400,2440
|
width(mm)
| 1200,1220 |
thickness(mm)
| 5,6,8,9,9.5,12,12.5,15,18 |
discrepancy of the thickness | 0±0.25 |
discrepancy of the diagonal | ≤3 |
5. Bried Introduction
The magnesium oxide board production line is highly automatic and
reduces
workforce. The products is formed one time. The products is smooth and uniformly.
The design production line is new on the idea,reasonable on
the structureand stable while working. The finished products
replaced of wooden
materials are more and more
recognized by people. The number of glass magnesium board used
grows more
and more. According to
authoritative forecast, the number of use of this material is
increasing 15% year by
year. Use of glass magnesium
board is the best way to protect forest resource and save trees, as
well as the best
alternative to wooden
decorative board.
1 | Air-dry density | ≤ (Standard index)50kg/m2 | (Test Value) 30.0kg/ m2 |
| 2 | Drying shrinkage rate of the board | ≤0.08% | 0.015% |
| 3 | Anti-breaking load | ≥1400N | 5640N |
| 4 | Anti-impact | No breakage phenomenon such as cracking after three impacts | No breakage phenomenon such as cracking after three impacts |
| 5 | Thermal resistance of main section (T=90mm) | ≥1.35(m2.k)/w | ≥1.36(m2.k)/w |
| 6 | Thermal bridges area ratio | ≤8% | 2.22% |
| 7 | Sound reduction Index | | 36dB |
| 8 | Radioactivity | | None
|