OhmAlloy-4J29 (Expansion alloy)
(Common Name: Kovar, Nilo K, KV-1, Dilver Po, Vacon 12)
OhmAlloy-4J29 also known as Kovar alloy. it was invented to meet the need for a reliable
glass-to-metal seal, which is required in electronic devices such
as light bulbs, vacuum tubes, cathode ray tubes, and in vacuum
systems in chemistry and other scientific research. Most metals
cannot seal to glass because their coefficient of thermal expansion
is not the same as glass, so as the joint cools after fabrication
the stresses due to the differential expansion rates of the glass
and metal cause the joint to crack.
OhmAlloy-4J29was invented to meet the need for a reliable
glass-to-metal seal, which is required in electronic devices such
as light bulbs, vacuum tubes, cathode ray tubes, and in vacuum
systems in chemistry and other scientific research. Most metals
cannot seal to glass because their coefficient of thermal expansion
is not the same as glass, so as the joint cools after fabrication
the stresses due to the differential expansion rates of the glass
and metal cause the joint to crack.
OhmAlloy-4J29 not only has thermal expansion similar to glass, but
its nonlinear thermal expansion curve can often be made to match a
glass, thus allowing the joint to tolerate a wide temperature
range. Chemically, it bonds to glass via the intermediate oxide
layer of nickel oxide and cobalt oxide; the proportion of iron
oxide is low due to its reduction with cobalt. The bond strength is
highly dependent on the oxide layer thickness and character. The
presence of cobalt makes the oxide layer easier to melt and
dissolve in the molten glass. A grey, grey-blue or grey-brown color
indicates a good seal. A metallic color indicates lack of oxide,
while black color indicates overly oxidized metal, in both cases
leading to a weak joint.
Application:Mainly used in electric vacuum components and emission control,
shock tube, igniting tube, glass magnetron, transistors, seal plug,
relay, integrated circuits lead, chassis, brackets and other
housing sealing.
Normal composition%
| Ni | 28.5~29.5 | Fe | Bal. | Co | 16.8~17.8 | Si | ≤0.3 |
| Mo | ≤0.2 | Cu | ≤0.2 | Cr | ≤0.2 | Mn | ≤0.5 |
| C | ≤0.03 | P | ≤0.02 | S | ≤0.02 | | |
Tensile Strength, MPa
| Code of condition | Condition | Wire | Strip |
| R | Soft | ≤585 | ≤570 |
| 1/4I | 1/4 Hard | 585~725 | 520~630 |
| 1/2I | 1/2 Hard | 655~795 | 590~700 |
| 3/4I | 3/4 Hard | 725~860 | 600~770 |
| I | Hard | ≥850 | ≥700 |
Typical Physical properties
| Density (g/cm3) | 8.2 |
| Electrical resistivity at 20℃(Ωmm2/m) | 0.48 |
| Temperature factor of resistivity(20℃~100℃)X10-5/℃ | 3.7~3.9 |
| Curie point Tc/ ℃ | 430 |
| Elastic Modulus, E/ Gpa | 138 |
Coefficient of expansion
| θ/℃ | α1/10-6℃-1 | θ/℃ | α1/10-6℃-1 |
| 20~60 | 7.8 | 20~500 | 6.2 |
| 20~100 | 6.4 | 20~550 | 7.1 |
| 20~200 | 5.9 | 20~600 | 7.8 |
| 20~300 | 5.3 | 20~700 | 9.2 |
| 20~400 | 5.1 | 20~800 | 10.2 |
| 20~450 | 5.3 | 20~900 | 11.4 |
Thermal conductivity
| θ/℃ | 100 | 200 | 300 | 400 | 500 |
| λ/ W/(m*℃) | 20.6 | 21.5 | 22.7 | 23.7 | 25.4 |
| The heat treatment process |
| Annealing for stress relief | Heated to 470~540℃ and hold 1~2 h. Cold down |
| annealing | In vacuum heated to 750~900℃ |
| Holding time | 14 min~1h. |
| Cooling rate | No more than 10 ℃/min cooled to 200 ℃ |
Style of supply
| Alloys Name | Type | Dimension | |
| OhmAlloy-4J29 | Wire | D= 0.1~8mm | |
| OhmAlloy-4J29 | Strip | W= 5~250mm | T= 0.1mm |
| OhmAlloy-4J29 | Foil | W= 10~100mm | T= 0.01~0.1 |
| OhmAlloy-4J29 | Bar | Dia= 8~100mm | L= 50~1000
|