Cutting Tools Tungsten Carbide Wear Plates High Thermal Conductivity

Tungsten steel is formed by pressing the powder into a billet, heating it to a certain temperature (sintering temperature) in a sintering furnace, and maintaining it for a certain period of time (heating time), and then cooling it down to obtain a tungsten steel material having desired properties.
The four basic stages of the tungsten steel sintering process:
1. Removal of the forming agent and the pre-firing stage, in which the sintered body undergoes the following changes:
The removal of the molding agent, as the temperature increases, the molding agent gradually decomposes or vaporizes at the initial stage of sintering, thereby eliminating the sintered body. At the same time, the molding agent more or less carbon is added to the sintered body, and the carbon addition amount will follow the molding agent. The type, quantity, and sintering process vary.
The surface oxide of the powder is reduced. At the sintering temperature, hydrogen can reduce the oxides of cobalt and tungsten. If the molding agent is removed by vacuum and sintered, the carbon-oxygen reaction is not strong. The contact stress between the powder particles is gradually eliminated, the bonded metal powder begins to recover and recrystallize, surface diffusion begins to occur, and the strength of the compact is improved.

2. Solid phase sintering stage (800 ° C - eutectic temperature)
At the temperature before the liquid phase appeared, in addition to the process that occurred in the previous stage, the solid phase reaction and diffusion were intensified, the plastic flow was enhanced, and the sintered body showed significant shrinkage.
3. Liquid phase sintering stage (eutectic temperature - sintering temperature)
When the sintered body exhibits a liquid phase, the shrinkage is quickly completed, followed by a crystallization transition to form the basic structure and structure of the alloy.
4, cooling stage (sintering temperature - room temperature)
At this stage, the microstructure and phase composition of tungsten steel vary with cooling conditions, and this feature can be utilized to heat treat tungsten steel to improve its physical and mechanical properties.

ZhuZhou Gold Sword Cemented Carbide Co., LTD.

ZhuZhou GoldSword Cemented Carbide Co.,LTD a rapid grow company expertise and professional in carbide materials and carbide cutting tools over 20 years of experience,integarated with new technology,high-end machinery and collaborated with researcher and university to enhance the cutting tool maker to make good quality tools for customer to reduce their cost gain more market share with us.

The company has advanced equipment a wide range of inspection equipment's to fulfil products quality inspection, using ERP system for production management and ordering processing , tracking and delivery, The company mission and vision are to help customer to reduce their cost and gain more market share with us.

Main products

carbide strips, carbide STB bars, carbide sand breaking strips, carbide ASA brazing tips, carbide cold heading dies and carbide rods, carbide cutting, carbide end mill carbide drill,carbide taps, wood working tool, wood cutting insert, carbide drill

bit saw blade and planer, planer reversible cutting insert carbide saw tips, solid carbide rod for metal & wood, advertising working tools, tungsten carbide perform tools like strips plate block.

Pressing Workshop

Sintering workshop 1

Sintering workshop 2

Processing workshop

Surface treatment workshop

Finishing workshop