SS 303 BRIGHT ROUND BARS GROUND FINISH 100%ULTRASONIC OK 303
Stainless Steel Round Bar
Stainless Steel - Grade 303 (UNS S30300)
Grade 303 represents the optimum in machinability among the
austenitic stainless steels. It is primarily used when production
involves extensive machining in automatic screw machines.
Machinability Rating (compared to B1212) is approximately 78%.
303 is also available as a "Ugima" Improved Machinability grade,
with machinability even higher than that of the standard 303.
The sulphur addition which is responsible for the improved
machining and galling characteristics of Grade 303 lowers its
corrosion resistance to below that of Grade 304. As for other
austenitic grades the structure gives 303 excellent toughness,
although the sulphur in 303 reduces its toughness slightly.
Grade 303Se (UNS S30323) has a selenium rather than sulphur
addition, improving the hot and cold forming characteristics over
those of 303 and providing a smoother machined surface finish. The
machinability rate is also slightly reduced. Grade 303Se is not
readily available in china
Key Properties
These properties are specified for long product (bar) in ASTM A582.
Similar but not necessarily identical properties are specified for
other products such as wire and forgings in their respective
specifications. Grade 303 is not produced in flat rolled products.
Composition
Typical compositional ranges for grade 303 stainless steels are
given in table 1.
able 1. Composition ranges for 303 grade stainless steel
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Se |
| 303 | min. max. | - 0.15 | - 2.00 | - 1.00 | - 0.20 | 0.15 - | 17.0 19.0 | - | 8.0 10.0 | - |
| 303Se | min. max. | - 0.15 | - 2.00 | - 1.00 | - 0.20 | 0.06 - | 17.0 19.0 | - | 8.0 10.0 | 0.15 min |
Mechanical Properties
Typical mechanical properties for grade 303 stainless steels are
given in table 2.
Table 2. Mechanical properties of 303 grade stainless steel
| Grade | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness |
| Rockwell B (HR B) | Brinell (HB) |
| 303 | - | - | - | - | 262 max |
Physical Properties
Typical physical properties for annealed grade 303 stainless steels
are given in table 3.
Table 3. Physical properties of 303 grade stainless steel in the annealed
condition
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) |
| 0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C |
| 303 | 8027 | 193 | 17.3 | 17.8 | 18.4 | 16.3 | 21.5 | 500 | 720 |
Grade Specification Comparison
Approximate grade comparisons for 303 stainless steels are given in
table 4.
Table 4. Grade specifications for 303 grade stainless steel
| Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS |
| BS | En | No | Name |
| 303 | S30300 | 303S31 | 58M | 1.4305 | X8CrNiS18-9 | 2346 | SUS 303 |
| 303Se | S30323 | 303S42 | - | - | - | - | SUS 303Se |
| These comparisons are approximate only. The list is intended as a
comparison of functionally similar materials notas a schedule of contractual equivalents. If exact equivalents are
needed original specifications must be consulted. |
Possible Alternative Grades
Possible alternative grades to grade 303 stainless steels are given
in table 5.
Table 5. Possible alternative grades to 303 grade stainless steel
| Grade | Why it might be chosen instead of 303 |
| 304 | Better corrosion resistance, formability or weldability are needed,
at the expense of lower machinability. |
| 316 | Higher resistance to pitting and crevice corrosion is required, in
chloride environments. A lower machinability can be accepted. |
| 416 | Even higher machinability than 303 is needed, and a lower corrosion
resistance can be tolerated. Or hardening by thermal treatment is required, while maintaining a
high machinability. |
Corrosion Resistance
Good resistance to mildly corrosive atmospheres, but significantly
less than Grade 304 due to the sulphur addition; the sulphide
inclusions act as pit initiation sites. Grade 303 should not be
exposed to marine or other similar environments, as these will
result in rapid pitting corrosion. Because the sulphide inclusions
in 303 are primarily aligned along the rolling direction the
corrosion resistance is particularly reduced in cross-sections.
Grade 303, like other common austenitic stainless steels, is
subject to stress corrosion cracking in chloride containing
environments above about 60°C.
Heat Resistance
Good oxidation resistance in intermittent service to 760°C and in
continuous service to 870°C. Continuous use in 425-860°C range not
usually recommended due to carbide precipitation - 303 usually does
not have a low carbon content so is susceptible to sensitisation.
Fabrication
As well as reducing the corrosion resistance, the sulphur additions
in 303 also result in poor weldability and reduced formability
compared to Grade 304. Sharp bends should not be
attempted in 303. A practical compromise alternative may be a 304
Ugima Improved Machinability grade - this does not machine as
readily as 303, but does offer better formability (as well as
better weldability and corrosion resistance).
Heat Treatment
Solution Treatment (Annealing) - Heat to 1010-1120°C and cool
rapidly. This grade cannot be hardened by thermal treatment.
Welding
Not generally recommended but, if unavoidable and a lower strength
can be tolerated, use Grade 308L or 309 electrodes. AS 1554.6 does
not pre-qualify welding of 303. Welds must be annealed for maximum
corrosion resistance.
Machining
A "Ugima" improved machinability version of grade 303 is available
in round bar products. This machines significantly better even than
standard 303, giving very high machining rates and lower tool wear
in many operations.