W.Nr 2.4654 age hardenable nickel alloy very good strength up to
980°C
W.Nr 2.4654 is an age hardening austenitic (face-centred cubic)
nickel-based superalloy. W.Nr 2.4654 is typically used in high
temperature applications, particularly in gas turbines.
Formerly Grade 685
W.Nr 2.4654 is an age-hardenable, nickel-based superalloy with
excellent strength properties through temperatures of roughly 980°C
(1800°F). Other characteristics of Waspaloy include good corrosion
resistance, as well as being relatively impervious to oxidation
making it well suited for service in extreme environments.
W.Nr 2.4654 has useful strength at temperatures up to 760-870°C
(1400-1600°F), and good oxidation resistance in gas turbine engine
atmospheres up to 870°C (1600°F). The creep rupture strength of
W.Nr 2.4654 is superior to that of Alloy 718 at temperatures above
620-650°C (1150-1200°F). Short time hot tensile strength is
inferior to RA718 at temperatures up to 730°C (1350°F).
Chemical composition (%)
Cr=18.00~21.00,
Mo=3.50~5.00,
Co=12.00~15.00,
Al=1.20~1.60,
Ti=2.75~3.25,
B=0.003~0.010,
C=0.020~0.100,
Zr=0.02~0.08,
Fe≤2.00,
Mn≤0.10,
Si≤0.15,
P≤0.015,
S≤0.015,
Cu≤0.10,
Ni=remainder
Specifications
AMS 5544, AMS 5708, AMS 5828, EN 2.4654, UNS N07001, Werkstoff
2.4654
Features
Excellent high-temperature strength and good resistance to
oxidation at a temperature up to 1800° F. This superalloy has
higher stability and strength ranges than those available for alloy
718.
Application
W.Nr 2.4654 is used for gas turbine engine components that call for
considerable strength and corrosion resistance at high operating
temperatures. Current and potential applications include compressor
and rotor discs, shafts, spacers, seals, rings and casings,
fasteners and other miscellaneous engine hardware, airframe
assemblies and missile systems