Use Black Phenolic Resin Plate For Enterprise Workshop Workbench
Through special processing of decorative color paper, reoccupy etch
steel at 150 ℃ high temperature 1430 psi high pressure environment,
through melting and irreversible aging hardening of 60 minutes a
integrated.
Comprehensive erosion resistance against acid and alkali, three
levels of protective structure:
1. The Chemical membrane Chemical - resistant qualities.
2. The color Paper Deco Paper;
3. Special multi-layer Kraft Paper (Kraft Paper).
1. Slab Size:
1220mm*2440mm ,1220mm*3050mm ,1220mm*3660mm
1525mm*3050mm ,1525mm*3660mm
Thickness: 12.7/16/19 mm
Surface:Matte
2. Product Description
Phenolic Resin Pane color is rich, have such as bright surface of
dumb light of a variety of surface texture, its surface after the
special chemical treatment has more powerful chemical resistance
performance.
Phenolic Resin Pane is a kind of specially made for laboratory stage face plate, by
more than 140 phenolic resin impregnated finest imported kraft
paper.
3. Acid resistance
| Test name | Test result | Grading result |
| 85% sulfuric acid | Specimen surface gloss and color no obvious change | Level 1 |
| 98% sulfuric acid | Specimen surface gloss and color no obvious change | Level 1 |
| 50% nitric acid | Specimen surface gloss and color no obvious change | Level 1 |
| 65% nitric acid | Specimen surface gloss and color no obvious change | Level 1 |
| 36% hydrochloric acid | Specimen surface gloss and color no obvious change | Level 1 |
| 85% phosphoric acid | Specimen surface gloss and color no obvious change | Level 1 |
| 40% hydrofluoric acid | Specimen surface gloss and color no obvious change | Level 1 |
| 60% chromic acid | Specimen surface gloss and color no obvious change | Level 1 |
| 99% glacial acetic acid | Specimen surface gloss and color no obvious change | Level 1 |
| Acetic acid | Specimen surface gloss and color no obvious change | Level 1 |
4.Physical Characteristics
| Mechanical Property | Test Standard | Test Result |
| Flexural Strength | MD | 205Mpa |
| Compressive Strength | MD | 321Mpa |
| Tensile Strength | MD | 178Mpa |
| IZOD Impact strength | CD | 102Mpa |
| ASTM D 256-06a | 42J/M |
| Flexural Modules | ASTM D 792-07 | 16.5Gpz |
| Rockwell Hardness | ASTM D 785-08 | HRE79.7 |
| Liquid Absorption | ASTM D 570-98 | 0.73% |