Low Melting Point Thermal Phase Changing Materials 0.95 W / mK with 0.024℃-in² / W

Low Melting Point Thermal Phase Changing Materials 0.95 W / mK with 0.024℃-in² / W

The TIC™803Y Series is low melting point thermal interface material. At 50℃, The TIC™800Y Series begins to soften and flow, filling the microscopic irregularities of both the thermal solution and the integrated circuit package surface, thereby reducing thermal resistance.The TIC™800Y Series is a flexible solid at room temperature and freestanding without reinforcing components that reduce thermal performance.

The TIC™803Y Series shows no thermal performance degradation after 1,000 hours@130℃,or after 500 cycles, from -25℃ to 125℃.The material softens and does not fully change state resulting in minimal migration (pump out)at operating temperatures.

Features:

Applications:

> High Frequency Microprocessors
> Notebook and Desktop PCs
> Computer Serves
> Memory Modules
> Cache Chips
> IGBTs

> Telecommunication

Standard Thicknesses:

0.003"(0.076mm) 0.005"(0.127mm) 0.008"(0.203mm) 0.010"(0.254mm)
Consult the factory alternate thickness.

Standard Sizes:

9" x 18"(228mm x 457mm) 9" x 400'(228mm x 121M)
TIC™800 series are supplied with a white release paper and a bottom liner. TIC™800 series is available in kiss cut an extended pull tab liner or individual die cut shapes.

Peressure Sensitive Adhesive:

Peressure Sensitive Adhesive is not applicable for TIC™800 series products.

Reinforcement:

No reinforcement is necessary.

Dongguan Ziitek Electronical Material and Technology Ltd. provides product solutions to equipment product which generates too much heat affecting its high performance when using. Plus thermal products can control and manage heat to keep it cool to some extent.  

Ziitek D-U-N-S® Number: 656191068