Neutral Cure Structural Liquid Waterproof Silicone Sealant for
Structural Bonding 300ml
Description:
Aristo Structural Silicone Sealant is a one-part, neutral cure,
specifically designed for structural bonding and curtain wall
adhesive construction applications. It easily extrudes in a wide
rang weather condition and quickly cures at room temperature to
form a high durable and flexible silicone rubber seal.
Applications:
1. Professional sealant for glass, glass device, big glass sheet;
2. Good for sealing among plastic-glass, aluminum-glass,
glass-glass etc;
3. Seal & cementation of al-alloy door & window, storefront, show
window, diagonal and skylight corner line;
4. Good sealing performance for glass, glass fiber, pottery &
porcelain and greaseless material
Specifications:
Product Name | Aristo Weatherproof Silicone Sealant |
Item | AA7309 |
Content | 300ml/pc |
Package | 24pcs/carton |
Carton Size | 310X210X240mm |
20ft Loading Capacity | 2000cartons/20'fcl |
Technical data sheet:
Structrual Silicone Sealant |
Performance | Standard | Measured Value | Testing Method |
Test at 50±5% RH and temperature 23±20C: |
Density (g/cm3) | ±0.1 | 0.96 | GB/T14683-2003 |
Tack-Free Time (min) | ≤180 | 5.5 | GB/T14683-2003 |
Extrusion (ml/min) | ≥80 | 1340 | GB/T14683-2003 |
Tensile Modulus (Mpa) | 23℃ | >0.4 | 0.48 | GB/T14683-2003 |
20℃ | or 0.6 | / |
Slumpability (mm) vertical | not change shape | not change shape | GB/T 14683-2003 |
Slumpability (mm) horizontal | ≤3 | 0 | GB/T 14683-2003 |
Curing Speed (mm/d) | 2 | 4 | / |
As Cured -After 21 days at 50±5% RH and temperature 23±20C: |
Hardness (Shore A) | 20~60 | 25 | GB/T14683-2003 |
Tensile Strength under Standard Conditions (Mpa) | / | 0.43 | GB/T14683-2003 |
Elongation of Rupture (%) | / | 41 | GB/T14683-2003 |
Movement Capability (%) | 12.5 | 12.5 | GB/T 14683-2003 |
Storage | over 12 Months |
Features:
1. Superior mildew-proofing, keep pleasing to the eyes and sanitary
in conditions of dark and high humidity.
2. Can be easily used and extruded any time.
3. Excellent adhesion to most building materials.
4. Excellent contact change and extrusion ability, in any air
temperature (-40C~100C) can extrude easily.