Perlite is one of nature’s most versatile and efficient minerals.
It is formed by molten (magma-tic) rock, also known as volcanic
glass. Over time, and during formation and cooling, water is
absorbed into the raw perlite ore matrix, giving perlite its unique
ability to expand when heated.
The expansion process renders the perlite partially transparent,
and the resulting complex refraction changes the color from a light
gray to bright white.
Hengyang Perlite Processing
Perlite is a glassy volcanic rock with a pearl-like luster. It
usually exhibits numerous concentric cracks that cause it to
resemble an onion skin. A typical perlite sample is composed of 71
to 75 percent silicon dioxide, 12.5 to 18.0 percent alumina, 4 to 5
percent potassium oxide, 1 to 4 percent sodium and calcium oxides,
and trace amounts of metal oxides.
Crude perlite ore is mined, crushed, dried in a rotary dryer,
ground, screened, and shipped to expansion plants.
Horizontal rotary or vertical stationary expansion furnaces are
used to expand the processed perlite ore. The normal size of crude
perlite expanded for use in plaster aggregates ranges from plus 250
micrometers (μm) (60 mesh) to minus 1.4 millimeters (mm) (12 mesh).
Crude perlite expanded for use as a concrete aggregate ranges from
1 mm (plus 16 mesh) to 0.2 mm (plus 100 mesh). Ninety percent of
the crude perlite ore expanded for horticultural uses is greater
than 841 μm
(20 mesh).
Crude perlite is mined using open-pit methods and then is moved to
the plant site where it is stockpiled. The first processing step is
to reduce the diameter of the ore to approximately 1.6 centimeters
(cm) (0.6 inch [in.]) in a primary jaw crusher. The crude ore is
then passed through a rotary dryer, which reduces the moisture
content from between 4 and 10 percent to less than 1 percent.
After drying, secondary grinding takes place in a closed-circuit
system using screens, air classifiers, hammer mills, and rod mills.
Oversized material produced from the secondary circuit is returned
to the primary crusher. Large quantities of fines, produced
throughout the processing stages, are removed by air classification
at designated stages. The desired size processed perlite ore is
stored until it is shipped to an expansion plant.
At the expansion plants, the processed ore is either preheated or
fed directly to the furnace. Preheating the material to
approximately 430EC (800EF) reduces the amount of fines produced in
the expansion process, which increases usable output and controls
the uniformity of product density. In the furnace, the perlite ore
reaches a temperature of 760 to 980EC (1400 to 1800EF), at which
point it begins to soften to a plastic state where the entrapped
combined water is released as steam. This causes the hot perlite
particles to expand 4 to 20 times their original size. A suction
fan draws the expanded particles out of the furnace and transports
them pneumatically to a cyclone classifier system to be collected.
The air-suspended perlite particles are also cooled as they are
transported to the collection equipment. The cyclone classifier
system collects the expanded perlite, removes the excessive fines,
and discharges gases to a bag house or wet scrubber for air
pollution control.