Moisture-Absorbing and Defoaming Masterbatch for Enhanced
Processing of Recycled Plastics
Technical Data of Desiccant Masterbatch
| Technical Data |
| Indicator | Value | Unit | Test Standard |
| Carrier Resin | Polyethylene |
| / |
| Functional Filler | Inorganic Absorbent |
| / |
| Density | 1.70 (±0.05) | g/cm3 | GB/T1033-86 B |
| Melt Flow Rate | <3.00 | g/10min (190℃/2.16Kg) | GB/T3682-2000 D |
| Water Content | <0.1 | % | IR |
| Filler Fineness | 800 | Mesh | Sieve Analysis |
| Particle Size | 4(+/-0.5) | mm | Micrometer Measurement |
| Processing Temperature | 140-220 | ℃ | / |
Recommended Addition Ratio
A dosage of 1–8% is suggested, which can be adapted according to
the moisture level in the recycled plastic material.
Product Overview
PE-200 is a multifunctional masterbatch formulated by compounding
an inorganic moisture-absorbing agent with a polyethylene carrier
through advanced manufacturing processes. It offers excellent
dispersibility, does not cause screen clogging, and ensures stable
processing performance.
This product provides a cost-efficient alternative to conventional
desiccant masterbatches available on the market, delivering
reliable moisture removal at a competitive price point.
PE-200 is suitable for use in recycled LLDPE, LDPE, HDPE, and PP
plastic products. It eliminates the need for pre-drying raw
materials, thereby reducing energy consumption and shortening
production cycles. By incorporating a small amount of PE-200,
processors can effectively resolve moisture-related issues,
minimize defects, and support the manufacturing of high-quality,
eco-friendly plastic end-products.