TA2 Industrial Pure Titanium Rod For Automotive And Energy Production

 Chemical Composition (Mass Fraction) / %                        

 Element                         

 Ti                      

 Al                      

 V                       

 Fe                      

 C                       

 N                       

 H                       

 O                       

 Other Single                    

 Other Total                     

 Minimum                         

 Balance                         

 Maximum                         

 Balance                         

 0.3                     

 0.1                     

 0.05                    

 0.015                   

 0.25                    

 0.1                     

 0.4                     

 Room Temperature Tensile Properties                     

 High Temperature Mechanical Properties                  

 Minimum                         

 Minimum                         

 Tensile Strength (Rm) / MPa                     

 440                     

 Tensile Strength (Rm) / MPa                     

 --                      

 Yield Strength (Rp0.2) / MPa                    

 320                     

 Test Stress (σ) / MPa                     

 -                       

 Elongation after Fracture (A) / %                       

 18                      

 Test Time (t) / h                       

 -                       

 Reduction of Area (Z) / %                       

 30                      

 Test Temperature / ℃                    

 -                       

 Alloy                   

 Condition                       

 Thickness Range/mm                      

 Tensile Strength (Rm)/MPa                       

 Yield Strength (Rp0.2)/MPa                      

 Elongation after Fracture /% ≥                       

 Bending Radius                  

 TA2                     

 M                       

 0.3 - 1.0                       

 440 - 620                       

 ≥320                         

 ≥35                  

 ≥100°, 3t                        

 > 1.0 - 2.0                  

 440 - 620                       

 ≥320                         

 ≥30                  

 ≥100°, 3t                        

 > 2 - 5.0                    

 440 - 620                       

 ≥320                         

 ≥25                  

 ≥90°, 3t                         

 > 5 - 10.0                   

 440 - 620                       

 ≥320                         

 ≥25                  

 -                       

 > 10.0 - 30                  

 440 - 620                       

 ≥320                         

 ≥18                  

 -                       

 TC4                     

 M                       

 0.5 - 1.8                       

 925 - 1150                      

 ≥870                         

 ≥12                  

 ≥105°, 9t                        

 > 1.8 - 4.0                  

 925 - 1150                      

 ≥870                         

 ≥12                  

 ≥105°, 10t                       

 > 4.0 - 5.0                  

 925 - 1150                      

 ≥870                         

 ≥10                  

 ≥105°, 10t                       

 > 5.0 - 10.0                         

 925 - 1150                      

 ≥825                         

 ≥10                  

 -                       

 > 10.0 - 100                         

 925 - 1150                      

 ≥825                         

 ≥9                   

 -                       

 Alloy                   

 Condition                       

 Thickness Range/mm                      

 Tensile Strength (Rm)/MPa                       

 Test Temperature/℃                      

 Test Stress(σ)/MPa                        

 Test Time(t)/h                  

 TC4                     

 M                       

 0.5 - 30.0mm                    

 ≥590                         

 400                     

 540                     

 ≥100                         

 ≥540                         

 500                     

 195