Introduction
WQ-P512 is a PTFE modified polyethylene wax powder.
Physical Property:
| Appearance | White Powder |
| Particle size (μm) | Dv50 7-9 |
| Particle size (μm) | Dv90 14 |
| Melting point (℃) | 112-120 |
Performance
As PE/PTFE composite micro-powder wax suitable for solvent-based
coatings and inks. The addition
of PTFE greatly improves the slippery and scratch resistance of
polyethylene wax micro-powder,
producing a very good synergistic effect.
Application
It can be utilized in flexographic printing ink, gravure printing
ink, and offset printing ink.
It can be incorporated into UV inks and UV coatings to offer
anti-settling, anti-adhesion, anti-scratch, anti-stain, and
anti-friction properties, while also delivering a smooth and soft
texture, as well as enhanced hydrophobicity and sealing
capabilities.
It can be applied in powder coatings of various resin systems such
as pure epoxy, epoxy polyester, and polyester TGIC, helping to
enhance surface hardness, smoothness, abrasion resistance, and
providing a certain matte finish.
Adding amount and using
In different systems, the amount of wax powder added is generally
between 0.5-3%.
It can usually be dispersed directly into solvent-based coatings
and inks by high-speed stirring.
It can be added through various grinders and high-shear dispersing
equipment. When using the
grinder, pay attention to controlling the grinding temperature.
Pre-dispersion treatment can be carried out to prepare a wax slurry
with a wax powder concentration
of 20-30%, which can be added to the system when needed, which can
reduce the dispersion time of
the wax powder.
Storage
This product is non-dangerous, please store it away from fire
sources and strong oxidants.
The shelf life is 24 months at room temperature.