Protect Your Environment with HDPE Textured Geomembrane in Sewage
Treatment Plants and More
Product Introduction
Spray Coarse Geosynthetics Membrane is a special geosynthetic
material. It is produced on the basis of the traditional production
process of polyethylene impervious membrane by updating the
production equipment, so that the surface of the produced
polyethylene impervious membrane forms a granular rough surface.
This design not only improves the friction performance of the
geomembrane surface, but also has stronger tensile strength
compared to the smooth membrane of the same specification.
Product Properties
Spray Rough Geomembrane has various performance characteristics
that make it excel in impervious engineering. Firstly, its
impermeability is highly reliable with a small permeability
coefficient, effectively preventing water seepage. Secondly, the
construction and laying are relatively easy, reducing construction
difficulty and cost. In addition, spray rough geomembrane has
strong tensile strength, elongation at break, and puncture
resistance, with stable material properties that can resist the
erosion of various chemical agents. The seams are connected by
double-seam hot welding, ensuring high seam strength and minimizing
leakage risks.
Application Fields
The application field of spray rough geotechnical membrane is very
extensive, mainly including the following aspects:
Landfill - Spray-coated geomembranes can be used for the impermeable layer
of landfills to control odor and reduce the generation of leachate.
Tailings Storage Facility: In tailings storage facilities, the spraying of rough geomembrane
can prevent harmful substances from leaking and protect the
environment.
Channel Imperviousness: Whether it's a water conveyance canal or an effluent river, the
grooved geomembrane can effectively prevent water loss.
Dam Seepage Prevention: In dam construction, shotcrete geosynthetic membrane can be used
as a seepage-proof layer to enhance the safety and stability of the
dam.
Subway Engineering: In subway engineering, waterproofing and seepage prevention also
require the support of shotcrete geotechnical membranes to ensure
the quality and safety of the project.
To sum up, the spray-coated geomembrane is a high-performance
impervious material suitable for various engineering fields, with
broad market demand and application prospects.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width: 4m~8m
* Roll length: 50m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Textured HDPE Geomembrane For Landfill (GB/T 17643-2011(GH-2T1,GH-2T2))
| Serial Number | Project | Index | | Thickness(mm) | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | | 1 | Density (g/c㎡,≥) | ≥0.940 | | 2 | Textured Highth (mm) | ≥0.25 | | 3 | Yield Strength (N/mm,LD/TD) | ≥11 | ≥15 | ≥18 | ≥22 | ≥29 | ≥37 | ≥44 | | 4 | Breaking Strength (N/mm,LD/TD) | ≥8 | ≥10 | ≥13 | ≥16 | ≥21 | ≥26 | ≥32 | | 5 | Yeild Elongation Rate (%) | ≥12 | | 6 | Breaking Elongation Rate (%) | ≥100 | | 7 | Rectangular Tear Strength (N) | ≥93 | ≥125 | ≥160 | ≥190 | ≥250 | ≥315 | ≥375 | | 8 | Puncture Strength (N) | ≥200 | ≥270 | ≥335 | ≥400 | ≥535 | ≥670 | ≥800 | | 9 | Tensile Load Stress Cracking (Notch Constant Load Tensle Method) h | ≥300 | | 10 | Carbon Black Content(Rang) (%) | 2.0~3.0 | | 11 | Carbon Black Dispersion | There is not more than one grade 3 in 10 data, and grade 4 and
grade 5 are not allowed | | 12 | Oxidative Induction Time (OIT) | Standard OIT (min)≥100 | | High Pressure OIT (min)≥400 | | 13 | 85℃ thermal aging (Atmospheric Pressure OIT Retention After 90 Day) | ≥55 | | 14 | Ultraviolet Irradiation After 1600 Hours, The OIT Retention(%) | ≥50 |
|
(CJ-T234-2006)
| Specification | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark |
| Item |
| Thickness (mm) | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | |
| Textured Highth (mm) | 0.25 | |
| Density (g/c㎡,≥) | 0.94 | |
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) | 15 | 18 | 22 | 29 | 37 | 44 | |
| Breaking Strength (N/mm,LD/TD) | 10 | 13 | 16 | 21 | 26 | 32 | |
| Yeild Elongation Rate (%) | 12 | |
| Breaking Elongation Rate (%) | 100 | |
| Rectangular Tear Strength (N) | 125 | 156 | 187 | 249 | 311 | 374 | |
| Puncture Strength (N) | 267 | 333 | 400 | 534 | 667 | 800 | |
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) | 300 | |
| Carbon Black |
| Carbon Black Content(Rang) (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more
than 1 of grade3 | |
| Oxidative Induction Time (OIT) |
| Standard OIT (min) | 100 | |
| High Pressure OIT (min) | 400 | |
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) | 55 | |
| 90 days after baking, the hight pressure OIT retention(%) | 80 | |
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT
retention(%) | 50 | |
| Ultraviolet irradiation after 1600 hours, the high pressure OIT
retention(%) | 50 | |
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | |
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | |
| Dimensional Stability | ±2 | |