High Capacity Anodizing Production Line with 300d/m x 20h/d Working
Hour
一.Product Description
1.Modern anodizing lines adopt functions such as closed-loop water
circulation, flue gas extraction, and wastewater treatment systems
to minimize environmental impact and comply with relevant
regulations.
2.The production line is equipped with advanced process control
systems and sensors to continuously monitor and adjust parameters
such as temperature, pH value, and current density, ensuring
consistent and high-quality results.
3.The aluminum anodizing line is highly automated, using a robotic
material handling system to move parts between various process
tanks and stations, improving efficiency, consistency, and worker
safety.
二. Design Condition
| 1 | Alloy | Aluminium 6061 to 6063 or others |
| 2 | Anodizing film thinkness | 10~ 12µm m |
| 3 | Average coverage area | 350m²/T (ton) |
| 4 | Max aluminium profile length | 6500mm |
| 5 | Extrusion ratio | 2.5kg/m² |
| 6 | Working hour/m | 300d/m x 20h/d = 600h/m |
| 7 | Racking system | Two fixtures /rack |
| 8 | Racking operation | Manual |
| 9 | Equipment Usage Rate | 0.9 |
| 10 | Power supply | AC 3phase 380v 50hz |
| 11 | Control Power | AC220V 50Hz |
| 12 | Water supply | 2kg/cm²·G |
| 13 | Hot steam | 6kg/cm²·G |
| 14 | Compressor air | 6kg/cm²·G |
三.Process Tank
| 1 | Degreasing 【Free sulfuric acid 180±30 g/l】 | 1 Tank |
| 2 | Alkaline Etching【Free alkali 40-60g/l,Al3+ 30-120g/】 | 2 Tanks |
| 3 | Neutralization 【Free sulfuric acid180±20g/l】 | 1 Tank |
| 4 | Anodising 【Free sulfuric acid 140-180g/l,Al3+≤20g/l】 | 4 Tanks |
| 5 | Colouring 【stannous sulfate 3-8g/l,Free sulfuric acid 15-25g/l,PH 0.8-1.2】 | 2 Tanks |
| 6 | Medium Temperature Sealing【PH 5-6.5,Nickel ion0.8-1.3g/l,Fluorion0.3-0.7 g/l】 | 3 Tank |
四.Treatment Process:
- Degreasing
(1) 6jig(rack)/ tank x 1 tank=6jig(rack)
(2) treatment time: 2-5min - Alkaline Etching
(1) 6jig(rack) / tank x 2 tank=12jig(rack)
(2) treatment time: 3-15min - Neutralization
(1) 6jig(rack) / tank x 1 tank=6jig(rack)
(2) treatment time: 1-5min - Anodizing
(1) 2 jig(rack)/tank x 4tanks = 8jig(rack)
(2) Current density: 130A/m²
(3) Process time: 30min
(4) Unprocess time: 10min
(5) Total time 30+10=40min
(6) Average anodizing layer : 0.3*1.3*30*0.77 =10.81um
- Colour 1
1) Clour process: Mix Salts
2) Quantity:2 jig(rack)/tank x 1tanks = 2jig(rack)
3) Current density: 70A
4) Process time: 2-8min
6. Sealing
1) Sealing menthod: Sealing at Medium or Normal Temperature
2) Quantity:6jig(rack)/tank x 1 tank
3) Process time 10-15min
五. Design Parameter and Setting
1. Anodizing treatment area:
1) Each anodizing process tank need 40min ,where total jig(rack)/year:
( 2 rack x 4 tank x 60min/h) ÷40min x600 hour =7200jig(rack)
2) Design 50m²/jig(rack) . Where every tank is 100m²
3) Area treatment/year : 7200jig(rack)x 50m² /jig =360000m²
2. Anodizing treatment weight:
Monthly output : 360000m²÷350m²/T*0.9=925T≧900T
3. Power consumption:
1) Anodising Tank:100m²/tank* 130A/ m²÷0.9=14444A/tank
Power Rectifier : 15000A =4unit
2) Clouring tank: 100㎡/tank×70A/m²÷0.9 = 7777A/tank
Colour Rectifier : 8000A =2unit
六. Process Chat
| Discription for Un |
| 1 | De | Degreasing |
| 2 | Rs | Rinsing |
| 3 | HW Rs | Hot Water Rinsing |
| 4 | AE | Alkaline Etching |
| 5 | Ne | Neutralization |
| 6 | An | Anodizing |
| 7 | Cl | Coloring |
| 8 | Sl | Sealing |
| 9 | MU | Material Unloading |
| 10 | Pc | Packing |