High Gloss Water Based Acrylic Emulsion Wood Coating Primer And
Topcoat Using
Introduction
WL-1049 is a high-performance self-crosslinking pure acrylic
core-shell polymer emulsion, it has high gloss and excellent
fullness,good flexibility, excellent weather resistance, water
resistance, scald resistance and chemical resistance, and it is
universal for the bottom and surface.
Specification
| Apperance | White Emulsion |
| Solid content (%) | 45±1 |
| Viscosity (CPS/25℃) | ＜1000 |
| pH | 7.5-8.5 |
| Particle size ( μm) | ＜25 |
| MFFT (℃) | 32 |
Formula
| Raw material | Added amount | Brand |
| WL-1049 | 80 | Wang Qin |
Tego902w | 0.2 | Tego |
DPNB | 3 | Dow |
DPM | 2 | Dow |
| Water | 13.9 | |
Tego270 | 0.2 | Tego |
PUR40 | 0.2 | METOLAT |
2020 | 0.2 | ACRYSOL |
Tego822 | 0.2 | Tego |
Cp15 | 0.1 | HOFMANN |
Properties
Low film forming temperature, suitable for low-end climate
construction.
Excellent water and chemical resistance.
Excellent resistance to yellowing and weathering.
Excellent flexibility, good adhesion, first choice for outdoor and
home decoration
Application
Excellent durability and high weather resistance wood paint,
Primer, varnish or pigment paint, used for outdoor and home
decoration
Packaging and Storage Condition
Package: 160 KG/Barrel, 1000KG IBC
Storage: Place in a cool ventilated place,keep container tightly
closed. Storage temperature is 3-35℃ .
Special Tips
This material is complied according to our existing technology and
experience, the technical advice provided is sincere, but it is not
guaranteed to be used in all samples and formulations, all the data
are for users reference only.