0Cr27Al7Mo2 is an iron-chromium-aluminium alloy (FeCrAl alloy) for
use at temperatures up to 1400°C (2552°F). The alloy with the
characteristics of high resistivity, low temperature coefficient of
electric resistance, high operating temperature, good oxidation
resistance under high temperature. It can equal to APM.
- Electric Furnace Heating Elements
In the industrial field, electric furnaces are widely used in
various heating processes, such as metal heating, glass
manufacturing, ceramic sintering, etc. 0Cr27Al7Mo2 resistance wire,
as the heating element of electric furnaces, can operate stably in
high-temperature environments, providing the required heating power
to efficiently heat the workpiece.
Resistance heaters are a common type of heating device that uses
the heat generated by passing current through resistance wire to
heat the workpiece. 0Cr27Al7Mo2 resistance wire is commonly used as
the heating element of resistance heaters due to its excellent
resistance characteristics and high temperature resistance, and it
can be widely used in industrial heating, laboratory research, and
other fields.
Electric heating tubes are devices that use the heat generated by
resistance wire to heat fluids or gases. 0Cr27Al7Mo2 resistance
wire is made into the heating core of electric heating tubes,
providing stable heating effects and widely used in household and
industrial equipment such as electric water heaters and electric
fans.
- Electric Melting Furnace Heating Elements
Electric heating is a common heating method in the process of metal
smelting. 0Cr27Al7Mo2 resistance wire is used as the electric
heating element of melting furnaces, providing high-temperature and
high-power heating effects to efficiently carry out metal smelting.
- Ferrous Chromium Aluminum alloy performance tables
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest |
| | | | | | Nb0.5 | Mo1.8-2.2 |
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | |
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |