Thermoplastic Road Marking Paint with Glass Beads Good Reflecitve
Fast Drying
Description
Thermoplastic road marking paint is mainly used for more than 2
level of the highway and highway, the marking coating thickness of
this paint is (1.0 ~ 2.5) mm, the paint is mixed with reflective
glass beads, and in the marking construction, the surface of the
reflective glass beads. This marking has good night reflective
performance, long service life, according to the traffic flow of
large highway construction of all kinds of road marking paint
demand estimates, small and the quality of the paint itself,
generally up to (2 ~ 3) years. The construction of hot melt coating
requires special heating equipment. For the second re-coating of
the old marking line, the thicker old coating should be removed
before coating.
Technical Specification
| Density(g/cm3) | 1.8-2.3 |
| Softening point (℃) | 90-125 |
| Compressive Strength(MPa) | ≥12 |
| Glass bead content(%) | 0-30% |
| Liquidity | 35±10 |
| Packing | 25kg/bag |
| Color | White/Yellow/Blue/Red/Green/Customized |
| Executive standard | JT/T280-2004/AASHTO/BS3262/Customized |
| Appearance | Powder |
| Construction temperature | 180℃-220℃ |
| Whiteness | 70-85(Customized) |
| Inverse coefficient | 50-550 |
| Warranty | 12 months |
| Storage Method | Avoid light and moisture |
| Packing Size | 45×70×5CM |
Main components and features
1. Titanium dioxide: Good whiteness, high purity, small particle
size, low oil absorption
2. C5 resin: Outstanding affinity for pigments, good compatibility
with EVA, good heat stability
3. PE wax: Heat resistance, abrasion resistance, as a lubricant,
increase paint processing performance.
4. Calcium carbonate: High precise classification, high whiteness
5. Glass beads: Drop on glass beads, intermix glass bead, we use
top brand beads brand, high reflective.
Formula Customized
| Customized Formula |
| Customized Formula | Content(Customized range) | Characteristics |
| C5 Resin | 10%-22% | Fluidity Toughness Hardness Adhesion |
| Titanium Dioxide | 0.5-10% | 0.5%-30% |
| Premixed glass beads | 0%-30% | Reflective after surface wear |
| Calcium Carbonate Sand | 30%-80% | Whiteness Wear-resistant Hardness |
| PE Wax | 1%-1.5% | Cold and heat resistant |
| EVA | 0.5%-1% | Crack resistance |
| Plasticizer | 1%-1.5% | Toughness |
Different Standards
| AASHTO Standard |
| Components | Specification | Test Result |
| Resin | ≥ 20% | 22% |
| Titanium Dioxide | ≥ 10% | 10.2% |
| Glass Beads | ≥ 30% | 32% |
| British Standard |
| Components | Specification | Test Result |
| Resin | ≥ 20% | 21% |
| Titanium Dioxide | ≥ 10% | 12% |
| Glass Beads | ≥ 20% | 21% |
| China Standard |
| Components | Specification | Test Result |
| Resin | ≥ 15% | 16.1% |
| Titanium Dioxide | ≥ 5% | 8% |
| Glass Beads | ≥ 20% | 22% |