ASTM A276 A473 TP 420 Heat Treated And Hardened Forged 20Cr13
Stainless Steel Bar
| Product | 420 Stainless Steel Round Rod |
| Grade | 200 Series: 201,202
300 Series: 304,304L,309,309s,310,310S,316,316L,316Ti,317L,321,347
400 Series: 409,409L,410,420,430,431,439,440,441,444
Others: 2205,2507,2906,330,660,630,631,17-4ph,17-7ph, S318039
904L,etc
Duplex stainless steel: S22053,S25073,S22253,S31803,S32205,S32304 |
| Standard | ASME, ASTM, EN, BS, GB, DIN, JIS etc |
| Technique | Cold Rolled, Hot Rolled, Forging |
| Surface | Annealed & Pickled, Bright, Polished, HL, Black |
| Size | Round Rod: Diameter: 3mm~800mm
Square Rod: 5x5mm - 200x200mm
Flat Bar: 20x2mm - 200x20mm
Hex Rod: 8mm - 200mm
Angle Bar: 20x20x2mm - 200x200x15mm |
| Packing | Bundled,wooden box for export standard package |
| Delivery Time | 7-15 days,or according to the order quantity or upon negotiation |
| MOQ | 500 KG |
Alloy 420 is a hardenable, martensitic stainless steel that is a
modification of Alloy 410. Similar to 410, it contains a minimum of
12% chromium, just sufficient enough to give corrosion resistant
properties. Alloy 420 has higher carbon content than Alloy 410
which is designed to optimize strength and hardness
characteristics. It has good ductility it the annealed condition
but is capable of being hardened to a minimum Rockwell hardness of
50 HRC, the highest hardness of the 12% chromium grades. Due to its
hardening properties, Alloy 420 is not often welded, although it is
possible. Martensitic stainless steels are designed for high
hardness and sometimes other properties are to some degree
compromised. Corrosion resistance is lower than the common
austenitic grades and their useful operating range is limited by
their loss of ductility at sub-zero temperatures and loss of
strength by over-tempering at elevated temperatures. Its best
corrosion resistance is achieved when the metal is hardened and
surface ground or polished.
Specifications: UNS S42000
Applications:
Alloy 420 is used for a variety of applications where good
corrosion and outstanding hardness is necessary. It is not usually
used at temperatures exceeding 800oF (427oC) due to quick hardening
and loss of corrosion resistance. Examples of applications that use
alloy 420 include:
- Cuttery
- Knife blades
- Surgical instruments
- Needle valves
- Shear blades
- Scissors
- Hand tools
Standards:
- ASTM/ASME: UNS S42000
- EURONORM: FeMi35Cr20Cu4Mo2
- DIN: 2.4660
Corrosion Resistance:
- Less resistant than the austenitic grades and the 17% chromium
ferritic alloys
- Good resistance in the hardened condition to the atmosphere, foods,
fresh water, and mild acids
- Resistance lowered in the annealed condition
- Best with a smooth surface finish
Heat Resistance:
- Not recommended for use above the relevant tempering temperature
because of reduction in mechanical properties
- Scaling temperature is approximately 1202oF (650oC)
Chemical Properties:
| C | Mn | Si | P | S | Cr |
|---|
| 420 | 0.15
max | 1.00
max | 1.00
max | 0.04
max | 0.03
max | min: 12.0
max: 14.0 |
FAQ
Q1. What are your company's main products ?
A1: Our main products are stainless steel plate/sheet, coil,
round/square pipe, bar, channel, etc.
Q2. Where is your factory ?
A2: Our company's processing center is located in Jiangsu, Wuxi,
China.
Which is well equipped with kinds of machines, such as laser
cutting machine,mirror polishing machine and so on.
We can provide a wide range of personalized services according to
the customers' needs.
Q3:How to confirm the Product Quality before placing orders?
A3:You can get free samples for some products,you only need to pay
the shipping cost or arrange a courier to us and take the samples.
The third-party will be accepted.
Q4. What are the advantages of your company ?
A4: We have many professionals, technical personnel, more
competitive prices and best after-dales service than other
stainless steel companies.
Q5. How many coutries you already exported ?
A5: Exported to more than 50 countries mainly from America, Russia,
UK, Kuwait, Egypt,Turkey, Jordan, India, etc.
Q6:What is your delivery time?
A6: For stocks, we could transport the goods to loading port within
7 days after we received your deposit
For production period, it usually takes about 15 days-30 days after
receiving the deposit.
Q7. Can you provide sample ?
A7: Small samples in store and can provide the samples for free.
Customized samples will take about 5-7days.