DESCRIPTION
Two Components Mold Making Silicone Rubber is generally named as
two-part silicone rubbers which vulcanise, or cure, at room
temperature. Part A is a dynamic liquid silicone/Part B is the
curing agent (tin catalyst).
APPLICATIONS
Two Components Mold Making Silicone Rubber can be used for
construction of moulds for gypsum, soap, candles, concrete, resin
products, artificial (very lightweight) stone, wax or custom
moulds;
Two Components Mold Making Silicone Rubber can be used for making
decorative building moulds (cornice, column, balustrade, ceilling
roses, pedestals, fountains, mantels, wall ornament, planter etc;
ADVANTAGES
Exceptional fluidity and good operability, easy to demold.
Cures at room temperature within 3-4 hours (assuming constant temp
of 25 degrees C).
Good tensile and tear strength, low shrinkage (<0.3%)
High duplication levels or longevity
Good resistance to weather, temperature, aging, acid.
Long shelf life (12 months at least) if kept at constant
temperatures.
STORAGE
Two Components Mold Making Silicone Rubber is an
environmentally-friendly liquid silicone product, is not easy to
burn and can be stored and transported as non-hazardous goods. The
shelf life of the product is about 12 months from the date of
production. Inspection is required when exceeding the time limited.
It can continue to be used in case of neither thickening nor
deterioration.
PACKAGE
Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 800g/bottle, 1kg/bottle
COMPANY INFORMATION
We are manufacturer, and specialized in manufacturing different
hardness, different viscosity silicone rubber series, we are
competitive in price with good quality.
Should you have any question, please feel free to contact us.
MINGCHENG GROUP LIMITED
| Item no. | MCSIL-H20 |
| Color | white |
| Viscosity | 25000±2000 cps |
| Mix ratio | 100:2 |
| Pot life | 30-40 mins |
| Curing time | 4-6 hrs |
| Hardness | 20 shore A |
| Tensile strength | 3.8 Mpa |
| Elongation | 600% |
| Tear Strength | 30 N/mm |
| Shrinkage | 0.3% |