High Performance 317L Stainless Steel Plate Alloy 317L SS Plate 1219mm 1500mm 2000mm Width

Alloy Structure and Composition

• Carbon (C): ≤ 0.03% (mitigates carbide precipitation, critical for intergranular corrosion resistance during welding).
• Chromium (Cr): 18–20% (forms a protective Cr₂O₃ layer against oxidation and general corrosion).
• Nickel (Ni): 11–15% (enhances toughness and resistance to reducing acids).
• Molybdenum (Mo): 3–4% (significantly boosts resistance to pitting and crevice corrosion in chloride-laden media, surpassing 316L).

Distinctive Mechanical Traits

1. Cold Workability: Maintains formability even after severe cold working, ideal for complex fabrications.
2. Temperature Stability:
   • Retains strength at sub-zero temperatures (down to -196°C), suitable for cryogenic applications.
   • Resists scaling up to 870°C, though prolonged exposure above 650°C may slightly reduce corrosion resistance.
3. Mechanical Values (Annealed):
   • Tensile Strength: 500–700 MPa
   • Yield Strength (0.2% offset): ≥ 205 MPa
   • Elongation: ≥ 45%

Corrosion Resistance Edge

• Chloride Environments: Excels in seawater, brine solutions, and paper pulping processes where chloride-induced pitting is a risk.
• Acid Resistance: Resists dilute sulfuric acid, formic acid, and acetic acid better than 300-series alloys.
• Crevice Corrosion: The higher Mo content shifts the crevice corrosion potential (Ecc) to more positive values, reducing vulnerability in stagnant or oxygen-depleted areas.

Innovative Applications

• Desalination Plants: Heat exchangers and pipelines in seawater desalination systems.
• Pharmaceutical Equipment: Reactors and tanks for handling corrosive APIs and cleaning agents (e.g., caustic soda and peroxide).
• Pollution Control: Scrubbers and ducts in flue gas desulfurization (FGD) systems exposed to sulfuric acid mist.
• Offshore Oil & Gas: Subsea valves, risers, and wellhead components in high-salinity, high-pressure environments.

Comparison with 316L

Manufacturing and Quality Control

• Welding: Gas Tungsten Arc Welding (GTAW) is preferred; use 317L filler metal to maintain corrosion resistance.
• Heat Treatment: Solution annealing at 1010–1120°C followed by water quenching to homogenize the structure.
• Testing: Commonly subjected to ASTM A923 testing for intergranular corrosion and ferritescope analysis to ensure a fully austenitic matrix.

Standards and Global Compliance

• ASTM A240 (Type 317L)
• EN 10088-2 (1.4438)
• JIS G4303 (SUS317L)
• ASME SA-240 for pressure vessel applications