High-performance silicon nitride ceramic materials developed for
the aluminum industry has significantly improved thermal and
mechanical properties than similar products. On this basis, the
"L-shaped high thermal conductivity submerged heating "Appliance"
will bring revolutionary progress to aluminum industrial equipment.
Special structural parts with high requirements for thermal shock
resistance are areas where silicon nitride ceramic materials can be
vigorously developed in the future. In application areas with high
temperature, strong corrosion, and high wear resistance, silicon
nitride ceramics are used to replace some cemented carbide,
alumina, Materials such as zirconia and silicon carbide will become
a trend.
Silicon Nitride Related Data
| Main component | 99%Al2O3 | S-SiC | ZrO2 | Si3N4 |
|
Physical
Property | Density | g/cm3 | 3.9 | 3.1 | 6 | 3.2 |
| Water Absorption | % | 0 | 0.1 | 0 | 0.1 |
| Sinter Temperature | °C | 1700 | 2200 | 1500 | 1800 |
Mechanical
Property | Rockwell Hardness | HV | 1700 | 2200 | 1300 | 1400 |
| Bend Strength | kgf/mm2 | 3500 | 4000 | 9000 | 7000 |
| Compression Intensity | Kgf/mm2 | 30000 | 20000 | 20000 | 23000 |
Thermal
Property | Maximum working
temperature | °C | 1500 | 1600 | 1300 | 1400 |
thermal expansion
coefficient
0-1000°C | /°C | 8.0*10-6 | 4.1*10-6(0-500°C) | 9.5*10-6 | 2.0*10-6(0-500°C) |
| 5.2*10-6(500-1000°C) | 4.0*10-6(500-1000°C) |
| Thermal Shock resistance | T(°C) | 200 | 250 | 300 | 400-500 |
| Thermal Conductivity | W/m.k(25°C | 31 | 100 | 3 | 25 |
| 300°C) | 16 | 100 | 3 | 25 |
Electrical
Property | Resisting rate of Volume | ◎.cm | | | | |
| 20°C | >1012 | 106-108 | >1010 | >1011 |
| 100°C | 1012-1013 | – | – | >1011 |
| 300°C | >1012 | – | – | >1011 |
Insulation Breakdown
Intensity | KV/mm | 18 | semiconductor | 9 | 17.7 |
| Dielectric Constant (1 MHz) | (E) | 10 | – | 29 | 7 |
| Dielectric Dissipation | (tg o) | 0.4*10-3 | – | – | – |