Excellent flowability and wettability braze powder joining metal
components
【 Main Application 】
Welding between metal parts
diamond brazing
【 Product advantage 】
One of the earliest research and production units of brazing
alloy powder in China, with a long history and mature technology,
customers all over the country
For different applications, different atomization technology is
used to ensure the best utilization value and cost performance of
powder.
Good sphericity of powder, controllable particle size
composition.
According to different requirements, some powder oxygen content
can be controlled below 200ppm.
【 Featured Products 】
Nickel base filler metal grades: BNi-2, BNi-7
Introduction: BNi-2 filler metal is the most widely used nickel
base high temperature filler metal. braze
In the process, it has good wettability, and the joint has
excellent oxidation resistance and corrosion resistance
Performance. Suitable for brazing stainless steel, heat-resistant
steel and superalloy working at high temperature
Parts. BNi-7 has the lowest melting temperature among nickel-based
brazing metals, 14% Cr element
At the same time, good heat resistance and corrosion resistance of
the filler metal were ensured. In the brazing process, BNi-7
The filler metal has excellent fluidity and can flow into
close-contact joints.
Copper base filler metal containing titanium grade: BCuSnTiIntroduction: CuSnTi filler metal is mainly used in brazing diamond
tools. Ti is a strong carbide active element and is also high
The strength of the connection element can generate TiC on the
diamond surface as an intermediate layer, improve the diamond
surface wettability, to improve
Combine strength for purpose.
Silver base filler metal grade: BAgCu28
Introduction: BAgCu28 filler metal is a kind of eutectic alloy
filler metal, alloy melting point
780℃, brazing process has good wettability, strong joint filling
ability, and can
Enough to form high strength, high conductivity and corrosion
resistance of brazing joints, widely used in electricity
Device welding, can also be used for brazing low carbon steel,
stainless steel, superalloy, copper and
Copper alloy, Var alloy and refractory alloy, etc.
| Name | Standard Designation | AWS Designation | Typical Component | Particle Size | Melting Temp. |
| Nickel based brazing powder | BNi73CrFeSiB (C) | BNi-1 | Cr14B3.1Si4.5Fe4.5C:0.7Ni bal. | -200
-300 | 980-1060 |
| BNi82CrSiBFe | BNi-2 | Cr7B3Si4.5Fe3Ni bal. | -200
-300 | 970-1000 |
| BNi92SiB | BNi-3 | B3Si4.5Ni bal. | -200
-300 | 980-1040 |
| BNi95SiB | BNi-4 | B1.8Si3.5Ni bal. | -200
-300 | 980-1070 |
| BNi71CrSi | BNi-5 | Crl9Sil0Ni bal. | -200
-300 | 1080-1135 |
| BNi76CrP | BNi-7 | Crl4P10Ni bal. | -200
-300 | 890 |
| BNi81CrB | BNi-9 | Crl5B3.5Ni bal. | -200
-300 | 1055 |
Copper base
braze
powder | BCu100 | BCu-1 | Cuz99.90 | -200
-300 | 1085 |
| BCu92P | | P8Cu bal. | -200
-300 | 710-770 |
| BCu60Zn | | Zn40Cu bal. | -200
-300 | 875-895 |
| BCuSn | | Sn20Cu bal. | -200
-300 | 800-930 |
| BCu86SnP | | Sn7P6.8Cu bal. | -200
-300 | 650-700 |
| BCuM nP | | Mn30P1Cu bal. | -200
-300 | 800-850 |
| BCu84MnNi | | Mn12Ni4Cu bal. | -200
-300 | 965-1000 |
| BCu85PSnNi | | Sn7P6.5Ni1.2Cu bal. | -200 | 612-682 |
| BCuSnTi | | Sn19Ti10Cu bal. | -250 | 900-960 |
Aluminium base
Brazing metal | BAI88Si | | Sil2Al bal. | -200 | 575-585 |
| BAI9OSi | | Si10Al bal. | -200 | 575-590 |
| BAI89SiMg | | Si10Mgl.5A1l bal. | -200 | 555-590 |
Silver base
Brazing metal | BAg72Cu | | Cu28Ag bal. | -300 | 779 |