20MNCr5 DIN1.7147 Alloy steel round bar
Round Bars: Dia.10 - 300mm with UT Assurance
Flat / Square Bars/Hex Bars:Thickness Max.600mm
Shafts, Rollers, Blocks: Customized or According to Drawing
20MnCr5 steel (DIN 1.7147 material)
20MnCr5 steel (1.7147 material) is an European standard carburized
steel (case hardening steel) with high strength and toughness and
good hardenability. The quenching deformation is small, the low
temperature toughness and the machinability are good, but the
welding performance is low. It's generally used after carburizing
quenching or quenching and tempering. (For specification and data
sheet, please see the tables below)
1.7147 steel is used to manufacture and reload large-section
tempered parts and small-section carburized parts. It can also be
used to manufacture medium and small parts with medium load and low
impact, such as gears, shafts, spindles, friction wheels and gears
of variable speed equipment, and the sleeve of the governor, etc.
(1.7147) 20MnCr5 Steel Chemical Composition
The chemical composition of 20MnCr5 steel are displayed in the
following table.
| | Chemical Composition % |
| Standard | Steel Grade | C | Si ≤ | Mn | P ≤ | S ≤ | Cr |
| EN 10084 | 20MnCr5
1.7147 | 0.17-0.22 | 0.40 | 1.10 to 1.40 | 0.025 | 0.035 | 1.00-1.30 |
| EN 10084 | 20MnCrS5
1.7149 | 0.17-0.22 | 0.40 | 1.10 to 1.40 | 0.025 | 0.020-0.040 | 1.00-1.30 |
Mechanical Properties of (20MnCr5) 1.7147 Steel
1.7147, 20MnCr5 Material Brinell hardness
- Treated for cold shearability: ≤ 255 HBW
- Soft annealed: ≤ 217 HBW
- Treated to hardness: 170-217 HBW
- Treated to ferrite-pearlite structure and hardness: 152-201 HBW
- Normalized: 140-201 HBW
20MnCr5, 1.7147 Tensile strength (after hardening and tempering at
200 °C)
- Dia. ≤ 16mm: Min. 1200 MPa
- 16 < Dia. ≤ 40mm: Min. 900 Mpa
- 40 < Dia. ≤ 100mm: Min. 700 Mpa
Heat Treatment Specification of 1.7147 Steel
- End quench test Austenitizing temperature: 870ºC (30-35 minutes)
- Carburizing temperature: 880-980 ºC
- Core-hardening temperature: 860-900 ºC
- Case-hardening temperature: 780-820 ºC
- Tempering: 150 - 200 ºC (≥ 1 hour)
Heat treatment:Quenched and Tempered (+QT), Normalizing (+N),
Annealing (+A)
Surface finish:Black / Rough turned / Peeled
Related Specifications
- ASTM/AISI:5120
- AFNOR:20MC5
- GB:20CrMn
- JIS:SMnC420
Quality Certification
A material test report(Inspection Certificate EN 10204 3.1) will be
provided, documenting the following:
1.Chemical analysis
2.Mechanical properties
3.Surface hardness
4.Non metallic inclusion
5.Heat treatment report
6.Grain size
7.Forging ratio
8.Ultrasonic test report