Tag Application High Strength Cross Laminated Packaging Film
Description:
It is a high-strength multi-layer composite film,It is made of HDPE
as the base material,
adding plasticizer, plasticizer, stabilizer, antioxidant, UV
absorber, toughener and other
additives through multi-layer co-extrusion blow molding into
embryos, and then by
multiple pull Stretching, then rotary cutting into a film substrate
with a horizontal and
vertical distribution of 45 °, and finally through
cross-compositing.
Due to its cross-stacking structure is different from ordinary
single-layer or multi-layer film,
it has the thermal stability, dimensional stability, two-way tear
resistance, two-way uniform
tension and high elongation which are not available in traditional
films.
Laminated film is an extremely versatile, high-performance product
line that resists tearing,
puncturing, and weathering. Our proprietary, cross-lamination
manufacturing process
provides considerably tighter gauge control than competitive spun
bonded, smoother
printing surfaces, and ease in converting. It is so strong that it
will not tear, even when
nicked, and withstands cold temperature. UV stabilized, the grades
hold up well during
outdoor exposure and provides superior moisture and chemical
resistance making
it ideal for engine tags as well as cruise and freight tags.
Advantages:
- Corona treated for optimal results when flexo, offset, or screen
printed, can also be thermal transfer printed (ANSI A Scans)
- Outdoor Durability: UV stabilized for improved weather resistance
and performance in harsh environments
- Performance in temperatures from -35°C-75°C
- Good ink adhesion: non-smearing
- Chemical and Oil Resistance
- Pre-printed or print-on-demand
- Excellent Staple Pullout Resistance
|
Application:
► Hanging and Labels
► Air Bag Covers
► EKG Labels (electrocardiogram)
► RFID (radio frequency identification)
► Law Labels
► Strength Tape
Tag Application High Strength Cross Laminated Packaging Film Phameter:
| NO. | Item | Performance |
| | SDM-30 | SDM-60 |
| 1 | Tensile Property | Tensile Strength/Mpa ≥ | 30 | 50 |
| | MaxF/(N/50mm) ≥ | 200 | 300 |
| | Elongation as MaxF/% ≥ | 200 |
| | Elongation at break/% ≥ | 250 |
| 2 | Sample number of no broken tested by free-falling dart method ≥ | 8 |
| 3 | Tear Strength(Nail Shank)/N ≥ | 60 |
| 4 | Angle Tear Strength/N ≥ | 25 |
| 5 | Thermal Stability | 120 ℃,10min, No bulb, No deformation |
| 6 | Cryogenic Flexibility ℃ | -35℃, No fissure, No delamination |
| 7 | Thermal Ageing | Appearance | No bulb, No deformation |
| | Subsequent MaxF/% ≥ | 80 |
| | Elongation at MaxF/% ≥ | 200 |
| | Elongation at break/% ≥ | 200 |
| 8 | Artificial Weathering | Appearance | No bulb, No deformation |
| | Subsequent MaxF/% ≥ | 70 |
| | Elongation at MaxF/% ≥ | 180 |
| | Elongation at break/% ≥ | 180 |
About Upass:
| Upass, founded in 2008, now as a governing unit of China Building
Waterproof Association, a vice chairman unit of Professional
Committee of China Modified Plastic Association, an enterprise with
Triple A credibility in China Plastic Association, not only assists
the development of the relevant industries, but also upholds the
conception of sustainable development by successive technological
innovation. Upass so far has acquired over 100 of intellectual
property rights. |
 |
 |
Our Team: