Beryllium Copper Tubing CLASS FOUR BERYLLIUM COPPER C17200 Tubes
Product Normal Description:
| Material Grade | RWMA Class Four, C17200 |
| Other Names | C172, CuBe2, DIN 2.1247, CW101C |
| End Product Form | Round Tubes |
| Standard | ASTM Standard |
| State of product | Hard, 1/2Hard |
| Application | Electrical Industry |
Introduction of Beryllium Copper (BeCu) Alloy C17200 Alloy 25:
Beryllium copper combines high strength with non-magnetic and
non-sparking qualities. It has excellent metalworking, forming, and
machining qualities. It has many specialized applications in tools
for hazardous environments, musical instruments, precision
measurement devices, bullets, and aerospace. Available in
small-order quantities, especially for engineering, die trials, and
short runs.
Beryllium Copper Pipes is an age-hardening alloy which attains the
highest strength of any copper base alloy. It may be age hardened
after forming into springs, intricate forms or complex shapes. It
has superb spring properties, corrosion resistance and stability as
well as good conductivity and low creep. Beryllium Copper Pipes has
excellent metalworking, forming and machining qualities. It has
many specialized applications in tools for hazardous environments,
musical instruments, precision measurement devices, bullets, and
aerospace. Beryllium-containing alloys create an inhalation hazard
during manufacturing due to their toxic properties.
Fabrication Properties of CLASS FOUR BERYLLIUM COPPER C17200 Alloy:
- Machining - C17200 copper alloy has a machinability rate of 20%.
- Welding - Butt welding, seam welding, spot welding, coated metal
arc welding, gas-shielded arc welding, brazing and soldering are
recommended for C17200 copper alloys.Oxyacetylene welding is not
recommended for C17200.
- Forging - For C17200 occurs at a temperature of 649 to 816 degrees
Celsius.
- Hot working - C17200 copper alloys have good hot working
capabilities.
- Cold working - C17200 copper alloys have excellent cold working
properties.
- Annealing - Is the process of heating metal or glass and allowing
it to cool slowly. This process removes internal stresses and
strengthens it. C17200 copper alloys are annealed at temperatures
from 774 to 802 degrees Celsius
Other fabrication properties include drawing, drilling, blanking,
forming and bending, tapping, and turning.
| C17200(CuBe2) |
| EN | ASTM | AMS | DIN | RWMA |
| CW101C | C17200 | 4533 | 2.1247 | RWMA Class 4 |
| | 4650 | | |
| | 4651 | | |
Chemical Composition of CLASS FOUR BERYLLIUM COPPER C17200 Alloy:
| Alloy number | Be | Ni Co | Ni Co Fe | Be Ni Co Fe Cu |
| C17200 / Alloy 25 | 1.8-2.0 | ≥0.2 | ≤0.6 | ≥99.5 |
Product Photo of CLASS FOUR BERYLLIUM COPPER C17200 Tubes:
Excellent Properties of CLASS FOUR BERYLLIUM COPPER C17200 Alloys: