1500 Degree U Shape Mosi2 Heating Elements Oxidation Resistance
Mosi2 Heating Elements introduction :
1. Mosi2 heating element is characterisized by excellent oxidation resistance and very good
form stability resulting in long element life. they are typically used in electrical heating
elements in industrial furnaces and home appliances.
2. Under the oxidizing atmosphere, the maximum operating
temperature is 1800, the resistance of the heating element of
silicon molybdenum rod increases rapidly with the temperature
increasing, and the resistance value is stable when the temperature
is constant.Under normal conditions, the resistance of elements
does not change with the service time, so the new and old elements
can be mixed.
Mosi2 Heating Elements Replacement
If there is a damaged part found in the process of operation, the
first thing you should do is determine its location and get all the
combination elements ready. After that, you should separate the
wire the damaged element clipped to from the screw which is
connected to the generatrix. Then remove the remained refractory
wool and pull out the refractory stoppers. Insert the new
combination elements into the furnace from its roof. Connect all
the wires and get the refractory wool filled, and finally raise the
temperature.
Physical property of molybdenum disilicide MoSi2 Rod Heater heating
element MoSi2 rod:
Volume Density | Bending Strength | Vickers Hardness | Porosity | Water absorption | Heating Elongation Rate |
5.5g/cm³ | 15-25kg/cm² | (HV)570kg/mm² | 7.4% | 1.2% | 4% |
Chemical Properties of Mosi2 Heating Elements
MoSi2 rod heater oxygen-resistance under high temperature: in
oxidizing atmosphere, a layer of compact quartz protective film is
formed on the surface of element owing to the high temperature
combustion, which prevent Mosi2 from oxidizing more. When the
element temperature is higher than 1700 °C, the film becomes
melting. It’s not suitable for long time use in the temperature
range of 400-700°C, otherwise, the element will be powdering for
the strong oxidation under low temperature.
Please tell us the following data of molybdenum disilicide MoSi2
rod heating element when send enquiry to us :
d = the diameter of hot zone ?
c = the diameter of cold zone ?
Le = the length of hot zone ?
Lu = the length of cold zone ?
a=Shank spacing
g=junction length
How many piece of MoSi2 rod heater do you need ?