SUS630 Cold Rolled Stainless Steel Strip In Coil ASTM A693 17-4PH
Martensitic precipitation/age-hardenable stainless alloy 630,
17-4PH, 1.4542, X5CrNiCuNb16-4 offers
high strength and hardness, excellent corrosion resistance, and
good fabricating characteristics.
Precipitation hardening steel 17-4PH is the most widely used of all
the precipitation-hardening stainless steels.
Its valuable combination of properties gives designers
opportunities to add reliability to their products
while simplifying fabrication and often reducing costs.
Applications
- Oil field equipment
- Chemical process equipment
- Fittings
- Pump shafts
- Gears
- Paper mill equipment
- Aircraft parts
- Flanges and valves
17-4PH is a martensitic precipitation-hardening stainless steel
that provides an outstanding combination
of high strength, good corrosion resistance, good mechanical
properties at temperatures up to 600°F (316°C),
good toughness in both base metal and welds, and short-time,
low-temperature heat treatments that
minimize warpage and scaling.
Composition ( % weight )
| C | Mn | P | S | Si | Cr | Ni | Cu | Nb |
| 0.07 max | 1.00 max | 0.040 max | 0.030 max | 1.00 max | 15.00~17.00 | 3.00~5.00 | 3.00~5.00 | 0.15~0.45 |
Delivery state
- Solution treated & Aged H1150
- Ultimate Tensile strength: 135 KSI min. ( 930 Mpa min. )
- Yield strength: 105 KSI min. ( 725 Mpa min. )
- Elongation: 8% min.
- Hardness: RC 38 max.
Typical Mechanical Properties
| Property | A | H900 | H925 | H1025 | H1075 | H1150 | H1150M |
| UTS | 1103 | 1448 | 1379 | 1276 | 1207 | 1103 | 1034 |
| YS | 1000 | 1379 | 1345 | 1172 | 1148 | 1034 | 896 |
| Elongation | 5.0 | 7.0 | 8.0 | 8.0 | 8.0 | 11.0 | 12.0 |
| Hardness, rockwell | C35 | C45 | C43 | C38 | C37 | C35 | C33 |
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless
ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com